Confinement effect on coercive field in relaxor terpolymer nanowires
Source abstract
Abstract
Abstract The confinement effect on the coercive field in relaxor ferroelectric poly(vinylidene fluoride-trifluoroethylene-chlorofluoroethylene)[P(VDF-TrFE-CFE)] terpolymer nanowires with different diameters ranging from 30 to 170 nm was studied using piezoelectric force microscope. It was found that the coercive field increases significantly as the diameter of terpolymer nanowires decreases. The results can be explained by the conversion of molecule conformation from T3G to Tm>4 in the terpolymer nanowires, which is supported by Fourier transform infrared spectroscope.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Dielectric materials and actuators · Advanced Sensor and Energy Harvesting Materials · Ferroelectric and Piezoelectric Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. Haberkorn · ACS Nano · 2009 · 3 · 141510.1021/nn900207a ↗
2. Gitsas · Nano Lett. · 2010 · 10 · 217310.1021/nl1009102 ↗
3. Berdichevsky · Adv. Mater. · 2006 · 18 · 12210.1002/adma.200501621 ↗
4. Grimm · J. Mater. Chem. · 2010 · 20 · 317110.1039/b926432a ↗
5. Hu · Nat. Mater. · 2009 · 8 · 6210.1038/nmat2339 ↗
6. Boesel · Adv. Mater. · 2010 · 22 · 212510.1002/adma.200903200 ↗
7. Freymann · Adv. Funct. Mater. · 2010 · 20 · 103810.1002/adfm.200901838 ↗
8. Dong · Adv. Funct. Mater. · 2006 · 16 · 193710.1002/adfm.200600225 ↗
9. Yang · Adv. Mater. · 2007 · 19 · 311910.1002/adma.200701956 ↗
10. Steinhart · Phys. Rev. Lett. · 2006 · 97 · 02780110.1103/PhysRevLett.97.027801 ↗
11. García-Gutiérrez · Nano Lett. · 2010 · 10 · 147210.1021/nl100429u ↗
12. Zhang · Science · 1998 · 280 · 210110.1126/science.280.5372.2101 ↗
13. Chu · Science · 2006 · 313 · 33410.1126/science.1127798 ↗
14. Xu · Appl. Phys. Lett. · 2001 · 78 · 236010.1063/1.1358847 ↗
15. Neese · Science · 2008 · 321 · 82110.1126/science.1159655 ↗
16. Bao · Macromolecules · 2007 · 40 · 237110.1021/ma062800l ↗
17. Guo · J. Nanosci. Nanotechnol. · 2014 · 14 · 208610.1166/jnn.2014.9272 ↗
18. Wang · Appl. Phys. Lett. · 2011 · 98 · 05290610.1063/1.3551732 ↗
19. Lin · Appl. Phys. Lett. · 2009 · 95 · 02291110.1063/1.3182786 ↗
20. Masuda · Science · 1995 · 268 · 146610.1126/science.268.5216.1466 ↗
21. Wang · Macromol. Rapid Commun. · 2008 · 29 · 72410.1002/marc.200800022 ↗
22. Hilczer · Ferroelectrics · 2011 · 417 · 12410.1080/00150193.2011.578528 ↗
23. Shingne · Polymer · 2013 · 54 · 273710.1016/j.polymer.2013.03.034 ↗
24. Urayama · Macromolecules · 2000 · 33 · 826910.1021/ma000855w ↗
25. Robels · J. Appl. Phys. · 1995 · 77 · 400210.1063/1.359511 ↗
26. Zhang · J. Appl. Phys. · 2006 · 99 · 04410710.1063/1.2169659 ↗
27. Tian · Appl. Phys. Lett. · 2015 · 106 · 09290210.1063/1.4913968 ↗
28. Liu · Appl. Phys. Lett. · 2014 · 104 · 22290710.1063/1.4881268 ↗
29. Tian · Appl. Phys. Lett. · 2013 · 102 · 07290610.1063/1.4793188 ↗
30. Lutkenhaus · Macromolecules · 2010 · 43 · 384410.1021/ma100166a ↗
31. Lando · Macromol. Sci., B: Phys. · 1968 · 2 · 20510.1080/00222346808212449 ↗
32. Bellet-Amalric · Eur. Phys. J. B · 1998 · 3 · 22510.1007/s100510050307 ↗
33. Abe · Polymer · 2001 · 42 · 340910.1016/S0032-3861(00)00794-1 ↗
34. Martin-Fabiani · ACS Appl. Mater. Interfaces · 2013 · 5 · 532410.1021/am401194p ↗
35. Jones · Macromolecules · 2001 · 34 · 55910.1021/ma001141o ↗