Effects of 850 °C annealing on near-surface defects in Mg-ion-implanted GaN examined using MOS structures

Genta Shindo, Yuki Hatakeyama, Hajime Fujikura, Shota Kaneki, Masafumi Yokoyama, Fumimasa Horikiri, Masamichi Akazawa

AIP Advances· Volume 15· Issue 8

Abstract

The effects of annealing at 850 °C on the near-surface defects in Mg-ion-implanted GaN were examined using subsequently formed metal–oxide–semiconductor structures. Here, Mg ions were implanted at 50 keV at a modest dose of 1.5 × 1011 or 1.5 × 1012 cm−2 into n-type GaN so as to not compensate fully for the doping density of 3.8 × 1017 cm−3 to maintain the n-type conduction of GaN for investigating the defect states near the conduction band. In the lower-dose sample, annealing at 850 °C for 30 min was effective in improving the capacitance–voltage (C–V) characteristics compared to those of the as-implanted samples. However, in the higher-dose sample, the improvement in the C–V characteristics was limited by acceptor-type defect states even after annealing at 850 °C for 60 min. Considering the results of the analysis of the interface state density distributions and doping profiles, we found that simple native defects were annealed out at 850 °C, whereas divacancy defects were detected even after annealing at 850 °C for up to 60 min. Nevertheless, the experimental results indicated the possibility that prolonging the annealing at 850 °C or raising the annealing temperature might lead to the elimination of divacancy defects through diffusion toward the GaN surface, where the vacancy defects can be distinguished.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: GaN-based semiconductor devices and materials · Semiconductor materials and devices · Semiconductor materials and interfaces

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Research Center for Integrated Quantum Electronics, Hokkaido University 1 , Kita 13, Nishi 8, Sapporo 060-0813,

Sumitomo Chemical Co., Ltd. 2 , Hitachi, Ibaraki 319-1418,

Funding

New Energy and Industrial Technology Development Organization · Japan Society for the Promotion of Science

References (46)

Show source-provided references
1. J. Appl. Phys. · 2021 · 129 · 18570210.1063/5.0050793 ↗
3. 2012 · 1
4. Appl. Phys. Express · 2008 · 1 · 01110510.1143/apex.1.011105 ↗
5. Appl. Phys. Lett. · 2016 · 109 · 16210410.1063/1.4965296 ↗
6. Appl. Phys. Express · 2018 · 11 · 12410210.7567/apex.11.124102 ↗
7. Jpn. J. Appl. Phys. · 2019 · 58 · SCCD0610.7567/1347-4065/ab09e0 ↗
8. Appl. Phys. Express · 2019 · 12 · 01100910.7567/1882-0786/aaf62a ↗
9. IEEE Electron Device Lett. · 2006 · 27 · 79610.1109/LED.2006.883054 ↗
10. Solid-State Electron. · 2008 · 52 · 15010.1016/j.sse.2007.07.035 ↗
11. Jpn. J. Appl. Phys. · 2008 · 47 · 778410.1143/jjap.47.7784 ↗
12. Appl. Phys. Express · 2017 · 10 · 12100410.7567/apex.10.121004 ↗
13. IEEE Trans. Electron Devices · 2018 · 65 · 427110.1109/ted.2018.2864260 ↗
14. Appl. Phys. Express · 2023 · 16 · 07400210.35848/1882-0786/ace33c ↗
15. 2024 · 4
16. Jpn. J. Appl. Phys. · 2014 · 53 · 10021010.7567/JJAP.53.100210 ↗
17. J. Cryst. Growth · 2012 · 350 · 2110.1016/j.jcrysgro.2011.12.016 ↗
18. Electron. Lett. · 2014 · 50 · 19710.1049/el.2013.3214 ↗
19. Phys. Status Solidi A · 2015 · 212 · 277210.1002/pssa.201532506 ↗
20. IEEE Trans. Semicond. Manuf. · 2016 · 29 · 34310.1109/tsm.2016.2600371 ↗
21. ECS Trans. · 2015 · 69 · 10510.1149/06911.0105ecst ↗
22. Nucl. Instrum. Methods Phys. Res., Sect. B · 2015 · 365 · 16810.1016/j.nimb.2015.07.095 ↗
23. Appl. Phys. Express · 2017 · 10 · 01650110.7567/apex.10.016501 ↗
24. Appl. Phys. Express · 2017 · 10 · 09100210.7567/apex.10.091002 ↗
25. Appl. Phys. Lett. · 2019 · 115 · 14210410.1063/1.5116866 ↗
26. Appl. Phys. Express · 2020 · 13 · 08650110.35848/1882-0786/aba64b ↗
27. Appl. Phys. Express · 2021 · 14 · 11100110.35848/1882-0786/ac2ae7 ↗
28. Appl. Phys. Express · 2021 · 14 · 05650110.35848/1882-0786/abf4f3 ↗
29. Appl. Phys. Express · 2021 · 14 · 12100410.35848/1882-0786/ac39b0 ↗
30. J. Appl. Phys. · 2022 · 132 · 13090110.1063/5.0107921 ↗
31. J. Appl. Phys. · 2018 · 123 · 20530310.1063/1.5029254 ↗
32. Phys. Status Solidi B · 2018 · 255 · 170052110.1002/pssb.201700521 ↗
33. Sci. Rep. · 2020 · 10 · 1734910.1038/s41598-020-74362-9 ↗
34. Phys. Status Solidi B · 2022 · 259 · 220018310.1002/pssb.202200183 ↗
35. Phys. Status Solidi B · 2020 · 257 · 190036710.1002/pssb.201900367 ↗
36. Jpn. J. Appl. Phys. · 2020 · 59 · 09650210.35848/1347-4065/abac41 ↗
37. Jpn. J. Appl. Phys. · 2021 · 60 · 01650210.35848/1347-4065/abcf08 ↗
38. AIP Adv. · 2022 · 12 · 12522410.1063/5.0117321 ↗
39. Jpn. J. Appl. Phys. · 2023 · 62 · SN100210.35848/1347-4065/ace3d1 ↗
40. Jpn. J. Appl. Phys. · 2023 · 62 · 12650110.35848/1347-4065/ad0272 ↗
41. Phys. Rev. B · 2004 · 69 · 03520710.1103/physrevb.69.035207 ↗
42. J. Cryst. Growth · 2016 · 448 · 7010.1016/j.jcrysgro.2016.05.007 ↗
43. J. Vac. Sci. Technol. B · 1986 · 4 · 113010.1116/1.583556 ↗
44. Appl. Surf. Sci. · 2008 · 254 · 800510.1016/j.apsusc.2008.03.051 ↗
45. Jpn. J. Appl. Phys. · 1993 · 32 · 51110.1143/jjap.32.511 ↗
46. Appl. Phys. Lett. · 2002 · 80 · 456410.1063/1.1485309 ↗