HgCdTe e-avalanche photodiode detector arrays

Initial results on the MWIR e-APD detector arrays with 30 μm pitch fabricated on LPE grown compositionally graded p-HgCdTe epilayers are presented. High dynamic resistance times active area (R0A) product 2 × 106 Ω-cm2, low dark current density 4 nA/cm2 and high gain 5500 at -8 V were achieved in the n+-υ-p+ HgCdTe e-APD at 80 K. LPE based HgCdTe e-APD development makes this technology amenable for adoption in the foundries established for the conventional HgCdTe photovoltaic detector arrays without any additional investment.