Investigation of AlGaN/GaN HEMTs degradation with gate pulse stressing at cryogenic temperature
Source abstract
Abstract
Degradation on DC characteristics of AlGaN/GaN high electron mobility transistors (HEMTs) after applying pulsed gate stress at cryogenic temperatures is presented in this paper. The nitrogen vacancy near to the AlGaN/GaN interface leads to threshold voltage of stress-free sample shifting positively at low temperature. The anomalous behavior of threshold voltage variation (decrease first and then increase) under gate stressing as compared to stress-free sample is observed when lowing temperature. This can be correlated with the pre-existing electron traps in SiNX layer or at SiNX/AlGaN interface which can be de-activated and the captured electrons inject back to channel with lowering temperature, which counterbalances the influence of nitrogen vacancy on threshold voltage shift.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: GaN-based semiconductor devices and materials · Semiconductor materials and devices · Silicon Carbide Semiconductor Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Electrical and Electronic Engineering, Southern University of Science and Technology 1 , Shenzhen 518055, China
Shenzhen Key Laboratory of 3rd Generation Semiconductor Devices 2 , Shenzhen 518055, China
Funding
shenzhen government, guangdong, P.R.CHINA · shenzhen government, guangdong,P.R.CHINA · shenzhen government,guangdong, P.R.CHINA · shenzhen government,guangdong,P.R.CHINA
References (32)
Show source-provided references
1. IEEE Trans. Electron. Devices · 2001 · 48 · 45010.1109/16.906435 ↗
2. J. Appl. Phys · 1999 · 85 · 688910.1063/1.370208 ↗
3. IEEE Electron.Dev.Lett · 2011 · 32 · 63210.1109/led.2011.2118190 ↗
4. 30W/mm GaN HEMTs by field plate optimization10.1109/led.2003.822667 ↗
5. Japan.J.Appl.Phys · 2016 · 55 · 05FK0610.7567/jjap.55.05fk06 ↗
6. Japan.J.Appl.Phys · 2016 · 55 · 04EG0110.7567/jjap.55.04eg01 ↗
7. Microeletron.Reliab · 2007 · 47 · 37210.1016/j.microrel.2006.01.012 ↗
8. Appl.Phys.Lett · 2013 · 103 · 19350710.1063/1.4829062 ↗
9. Microeletron.Reliab · 2016 · 58 · 15110.1016/j.microrel.2015.11.024 ↗
10. Phys. Status. Solidi A · 2015 · 212 · 112210.1002/pssa.201431744 ↗
11. 2012 10–13, 2012 · 13.1.1
12. IEEE Trans. Electron.Devices · 2014 · 61 · 102210.1109/ted.2014.2303853 ↗
13. IEEE Electron. Device Letters · 2013 · 34 · 111210.1109/led.2013.2272095 ↗
14. Appl.Phys.Lett · 2014 · 105 · 03351210.1063/1.4891532 ↗
15. J.Vac.Sci.Technol.B · 2017 · 34 · 041202–1
16. IEEE Trans. Electron.Devices · 2017 · 64 · 82410.1109/ted.2017.2654358 ↗
17. Appl. Phys. Lett · 2010 · 96 · 01350510.1063/1.3275754 ↗
18. Semicond.Sci.Technol · 2017 · 32 · 02501710.1088/1361-6641/aa5253 ↗
19. IEEE Trans. Device Mater. Reliab · 2010 · 10 · 42710.1109/tdmr.2010.2072507 ↗
20. Appl. Phys. Lett · 2014 · 105 · 01350410.1063/1.4887368 ↗
21. Chin. Phys. B · 2013 · 22 · 01720210.1088/1674-1056/22/1/017202 ↗
22. IEEE Electron.Device.Lett · 2005 · 26 · 71010.1109/led.2005.856709 ↗
23. Appl.Phys.Lett · 2007 · 90 · 12350510.1063/1.2715032 ↗
24. 1989
25. 1998
26. IEEE.Trans.Electron.Dev · 1995 · 42 · 12310.1109/16.370026 ↗
27. J. Appl.Phys · 2008 · 103 · 10451010.1063/1.2924334 ↗
28. Appl. Phys. Lett · 2002 · 80 · 218610.1063/1.1461420 ↗
29. Thin.Solid.Films · 2007 · 515 · 451710.1016/j.tsf.2006.07.168 ↗
30. AIP.Advance · 2016 · 6 · 09502110.1063/1.4963740 ↗
31. IEEE.Trans.Electron.Dev · 2015 · 62 · 53210.1109/ted.2014.2380354 ↗
32. Acta.Physica.Polonica.A · 2001 · 119 · 19610.12693/aphyspola.119.196 ↗