Growth of Ca, Zr co-doped BaTiO3 lead-free ferroelectric single crystal and its room-temperature piezoelectricity

Lead-free Ca, Zr co-doped BaTiO3 (BCZT) single crystal with a dimension up to 2mm×2mm×2mm was grown by a spontaneous nucleation technique using KF as the flux. The composition of the studied single crystal was defined to be Ba0.798Ca0.202Zr0.006Ti0.994O3, corresponding to a tetragonal phase at room temperature. The <001> oriented single crystal exhibited a quasi-static piezoelectric constant of approximately 232 pC/N. The effective piezoelectric coefficient d33* of the single domain crystal obtained under a unipolar electric field of 35 kV/cm was 179 pm/V. Rayleigh analysis was used to identify the intrinsic and extrinsic contributions to the room-temperature piezoelectricity of BCZT single crystal. The extrinsic contribution was estimated up to 40% due to the irreversible domain wall movement. Furthermore a sixth-order polynomial of Landau expansion was employed to analyze the intrinsic contribution to piezoelectricity of BCZT single crystal. The large energy barriers inhibited polarization rotations, leading to the relatively low piezoelectricity.