Activation energy of metastable amorphous Ge2Sb2Te5 from room temperature to melt
Source abstract
Abstract
Resistivity of metastable amorphous Ge2Sb2Te5 (GST) measured at device level show an exponential decline with temperature matching with the steady-state thin-film resistivity measured at 858 K (melting temperature). This suggests that the free carrier activation mechanisms form a continuum in a large temperature scale (300 K – 858 K) and the metastable amorphous phase can be treated as a super-cooled liquid. The effective activation energy calculated using the resistivity versus temperature data follow a parabolic behavior, with a room temperature value of 333 meV, peaking to ∼377 meV at ∼465 K and reaching zero at ∼930 K, using a reference activation energy of 111 meV (3kBT/2) at melt. Amorphous GST is expected to behave as a p-type semiconductor at Tmelt ∼ 858 K and transitions from the semiconducting-liquid phase to the metallic-liquid phase at ∼ 930 K at equilibrium. The simultaneous Seebeck (S) and resistivity versus temperature measurements of amorphous-fcc mixed-phase GST thin-films show linear S-T trends that meet S = 0 at 0 K, consistent with degenerate semiconductors, and the dS/dT and room temperature activation energy show a linear correlation. The single-crystal fcc is calculated to have dS/dT = 0.153 μV/K2 for an activation energy of zero and a Fermi level 0.16 eV below the valance band edge.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Phase-change materials and chalcogenides · Chalcogenide Semiconductor Thin Films · Nonlinear Optical Materials Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Electrical and Computer Engineering, University of Connecticut 1 , Storrs, Connecticut 06269, USA
Department of Electrical and Electronics Engineering, Eskisehir Osmangazi University 2 , Eskisehir 26480, Turkey
Department of Electrical and Electronics Engineering, Atilim University 3 , Ankara 06830, Turkey
IBM Watson Research Center 4 , Yorktown Heights, New York 10598, USA
Funding
Division of Electrical, Communications and Cyber Systems · Air Force Office of Scientific Research · Basic Energy Sciences
References (29)
Show source-provided references
1. IEEE Trans. Electron Devices · 2017 · 64 · 437410.1109/ted.2017.2746342 ↗
2. Nat. Mater. · 2007 · 6 · 82410.1038/nmat2009 ↗
3. Nat. Mater. · 2004 · 3 · 70310.1038/nmat1215 ↗
4. IEEE J. Emerg. Sel. Top. Circuits Syst. · 2016 · 6 · 14610.1109/jetcas.2016.2547718 ↗
5. J. Appl. Phys. · 2017 · 122 · 12510410.1063/1.4996218 ↗
6. Rev. Sci. Instrum. · 2016 · 87 · 07511710.1063/1.4959222 ↗
7. Appl. Phys. Lett. · 2011 · 98 · 24350610.1063/1.3599559 ↗
8. Nanoscale · 2015 · 7 · 1662510.1039/c5nr05512a ↗
9. 2006 · 1
10. J. Appl. Phys. · 2007 · 102 · 05451710.1063/1.2773688 ↗
11. Front. Phys. · 2014 · 2 · 7510.3389/fphy.2014.00075 ↗
12. J. Appl. Phys. · 2012 · 112 · 08450610.1063/1.4759239 ↗
13. J. Appl. Phys. · 2009 · 105 · 08450610.1063/1.3109063 ↗
14. IEEE Electron Device Lett. · 2010 · 31 · 102310.1109/led.2010.2052016 ↗
15. Electron Devices, IEEE Trans. · 2013 · 60 · 43310.1109/ted.2012.2228273 ↗
16. Chem. Rev. · 1948 · 43 · 21910.1021/cr60135a002 ↗
17. 2017
18. Sci. Rep. · 2013 · 3 · 272410.1038/srep02724 ↗
19. Electron Devices, IEEE Trans. · 2014 · 61 · 37210.1109/ted.2013.2296305 ↗
20. 2014 · HH3.02
21. Jpn. J. Appl. Phys. · 2010 · 49 · 06580210.1143/jjap.49.065802 ↗
22. Jpn. J. Appl. Phys. · 2005 · 44 · 734010.1143/jjap.44.7340 ↗
23. Phys. Rev. Appl. · 2017 · 7 · 03403510.1103/physrevapplied.7.034035 ↗
24. J. Appl. Phys. · 2005 · 97 · 09350910.1063/1.1884248 ↗
25. F. Dirisaglik, Ph.D. thesis, University of Connecticut, Storrs, CT, 2014.
26. Sci. Rep. · 2016 · 6 · 3169910.1038/srep31699 ↗
27. J. Non. Cryst. Solids · 2010 · 356 · 217210.1016/j.jnoncrysol.2010.07.039 ↗
28. Appl. Phys. Lett. · 2007 · 90 · 17192010.1063/1.2722203 ↗
29. 1993 · 44