Study of the crystal structure of SnS thin films by atomic layer deposition

Tin monosulfide, SnS, absorbs visible light and holds promise for thin-film photovoltaics. However, the optoelectronic properties of this material vary among the different structural phases, and control over the phase of vapor deposited SnS thin films is not well understood. In order to study the phases and crystallographic orientations of SnS films, films with thicknesses of 90 nm–750 nm were prepared by atomic layer deposition (ALD) at temperatures between 80 °C and 200 °C on amorphous silicon dioxide (a-SiO2) and single-crystal sodium chloride (NaCl). We show that the crystal structures and orientations of the ALD-SnS thin films vary with deposition temperature, film thickness, and substrate. We confirm the presence of metastable cubic π-SnS in co-existence with the thermodynamically stable orthorhombic α-SnS and find that the π phase is more prevalent at lower deposition temperatures. The films grown on a-SiO2 are textured, the degree of texturing increases with lower temperature or higher thickness, and the deposited phase is also thickness dependent. Upon annealing, which is known to promote SnS grain growth, all films revert to orthorhombic α-SnS. The films grown on the NaCl(100) substrate exhibit a much higher degree of texturing and show different preferred orientations dependent on the phase: π-(400) and α-(111) or α-(040). In addition, we demonstrate a proof-of-concept device made from the highly oriented SnS grown on NaCl.