Control of O-H bonds at a-IGZO/SiO2 interface by long time thermal annealing for highly stable oxide TFT
Source abstract
Abstract
We report two-step annealing, high temperature and sequent low temperature, for amorphous indium-gallium-zinc-oxide (a-IGZO) thin-film transistor (TFT) to improve its stability and device performance. The annealing is carried out at 300 oC in N2 ambient for 1 h (1st step annealing) and then at 250 oC in vacuum for 10 h (2nd step annealing). It is found that the threshold voltage (VTH) changes from 0.4 V to -2.0 V by the 1st step annealing and to +0.6 V by 2nd step annealing. The mobility changes from 18 cm2V-1s-1 to 25 cm2V-1s-1 by 1st step and decreases to 20 cm2V-1s-1 by 2nd step annealing. The VTH shift by positive bias temperature stress (PBTS) is 3.7 V for the as-prepared TFT, and 1.7 V for the 1st step annealed TFT, and 1.3 V for the 2nd step annealed TFT. The XPS (X-ray photoelectron spectroscopy) depth analysis indicates that the reduction in O-H bonds at the top interface (SiO2/a-IGZO) by 2nd step annealing appears, which is related to the positive VTH shift and smaller VTH shift by PBTS.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Thin-Film Transistor Technologies · Silicon and Solar Cell Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Advanced Display Research Center (ADRC), Department of Information Display, Kyung Hee University , 26, Kyungheedae-ro, Dongdaemun-gu, Seoul 02447, Korea
Funding
MOTIE | Korea Evaluation Institute of Industrial Technology
References (26)
Show source-provided references
1. Nature · 2004 · 432 · 48810.1038/nature03090 ↗
2. J. Disp. Technol. · 2009 · 5 · 27310.1109/jdt.2009.2021582 ↗
3. Sci. Technol. Adv. Mater. · 2010 · 11117 · 44305
4. Japanese J. Appl. Physics, Part 1 Regul. Pap. Short Notes Rev. Pap. · 2006 · 45 · 430310.1143/jjap.45.4303 ↗
5. Adv. Mater. · 2012 · 24 · 294510.1002/adma.201103228 ↗
6. Appl. Phys. Lett. · 2007 · 9010.1063/1.2723543 ↗
7. Appl. Phys. Lett. · 2011 · 99 · 06210810.1063/1.3615304 ↗
8. Appl. Phys. Lett. · 2013 · 102 · 02350310.1063/1.4775694 ↗
9. Appl. Phys. Lett. · 2009 · 95 · 06350210.1063/1.3187532 ↗
10. Appl. Phys. Lett. · 2012 · 10110.1063/1.4752238 ↗
11. ECS J. Solid State Sci. Technol. · 2013 · 2 · P510.1149/2.011301jss ↗
12. Appl. Phys. Lett. · 2011 · 98 · 10350910.1063/1.3564882 ↗
13. J. Appl. Phys. · 2013 · 113 · 06371210.1063/1.4792229 ↗
14. Appl. Phys. Lett. · 2009 · 95 · 01350710.1063/1.3167816 ↗
15. J. Disp. Technol. · 2016 · 12 · 26310.1109/jdt.2015.2475127 ↗
16. J. Appl. Phys. · 2015 · 117 · 23450210.1063/1.4922714 ↗
17. IEEE Trans. Electron Devices · 2016 · 63 · 191010.1109/ted.2016.2545742 ↗
18. J. Electroceramics · 2012 · 28 · 7410.1007/s10832-011-9680-5 ↗
19. Appl. Phys. Lett. · 2011 · 99 · 08210410.1063/1.3623426 ↗
20. Appl. Phys. Lett. · 2009 · 95 · 01350310.1063/1.3159831 ↗
21. Nat. Mater. · 2007 · 6 · 4410.1038/nmat1795 ↗
22. IEEE Trans. Electron Devices · 2012 · 59 · 250110.1109/ted.2012.2205258 ↗
23. Appl. Phys. Lett. · 2013 · 10210.1063/1.4801762 ↗
24. Appl. Phys. Lett. · 2014 · 10510.1063/1.4903874 ↗
25. J. Mol. Spectrosc. · 1997 · 183 · 3410.1006/jmsp.1996.7237 ↗
26. Appl. Phys. Lett. · 2017 · 11010.1063/1.4985627 ↗