Dynamic Nanoscale Spatial Heterogeneity in a Perovskite-to-Brownmillerite Topotactic Phase Transformation

Phase transitions are omnipresent in modern condensed matter physics and its applications. In solids, first-order phase transformations typically occur by nucleation and growth under nonequilibrium conditions. Under constant external conditions, e.g., constant annealing temperature and pressure, the nucleation and growth dynamics are often thought of as spatially and temporally independent. Here, in situ Bragg X-ray photon correlation spectroscopy (XPCS) reveals nanoscale spatial and dynamical heterogeneity in the perovskite-to-brownmillerite topotactic phase transformation in La 0.7 Sr 0.3 CoO 3 thin films annealed under constant reducing conditions over a time span of multiple hours. Specifically, a time scale associated with domain growth remains stable, with a corresponding domain wall speed of v d = 6 ± 0.5 × 10 –4 nm/s (2 ± 0.2 nm/h), while a slower time scale, associated with temperature-driven depinning of domains, leads to accelerating dynamics with time scales following an aging power law with exponent −2.2 ± 0.5. This experiment demonstrates that Bragg XPCS is a powerful tool to study nanoscale dynamics in structural phase transformations, with the ability to extract quantitative average values related to nanodomain motion in situ . The results are relevant for phase engineering of phase-change devices, as they show that nanoscale dynamics, linked to domain and domain-wall motion, can continuously evolve and speed up with time, even hours after the initiation of the phase transformation, with potential repercussions on electrical performance.