Defect-Free Erbium Silicide Formation Using an Ultrathin Ni Interlayer
Source abstract
Abstract
An ultrathin Ni interlayer (∼1 nm) was introduced between a TaN-capped Er film and a Si substrate to prevent the formation of surface defects during thermal Er silicidation. A nickel silicide interfacial layer formed at low temperatures and incurred uniform nucleation and the growth of a subsequently formed erbium silicide film, effectively inhibiting the generation of recessed-type surface defects and improving the surface roughness. As a side effect, the complete transformation of Er to erbium silicide was somewhat delayed, and the electrical contact property at low annealing temperatures was dominated by the nickel silicide phase with a high Schottky barrier height. After high-temperature annealing, the early-formed interfacial layer interacted with the growing erbium silicide, presumably forming an erbium silicide-rich Er-Si-Ni mixture. As a result, the electrical contact property reverted to that of the low-resistive erbium silicide/Si contact case, which warrants a promising source/drain contact application for future high-performance metal-oxide-semiconductor field-effect transistors.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Semiconductor materials and interfaces · Silicon Nanostructures and Photoluminescence · Semiconductor materials and devices
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon 440-746, Republic of Korea
Institute of Physics and Applied Physics, Yonsei University, Seoul 120-749, Republic of Korea
Funding
Korea Evaluation Institute of Industrial Technology
References (19)
Show source-provided references
1. Reckinger N. · J. Appl. Phys. · 2008 · 104 · 10352310.1063/1.3010305 ↗
2. Kuroda R. · IEEE Int. Electron Devices Meet., Technol. Dig. · 2010 · 580
3. Tang X. · Solid-State Electron. · 2003 · 47 · 210510.1016/S0038-1101(03)00256-9 ↗
4. Wu C. S. · Thin Solid Films · 1983 · 104 · 17510.1016/0040-6090(83)90559-X ↗
5. Tsai W. C. · J. Appl. Phys. · 2004 · 96 · 535310.1063/1.1769604 ↗
6. Tu K. N. · Appl. Phys. Lett. · 1981 · 38 · 62610.1063/1.92457 ↗
7. Huang W. · Thin Solid Films · 2008 · 516 · 425210.1016/j.tsf.2007.12.154 ↗
8. Tan E. J. · Appl. Phys. Lett. · 2006 · 88 · 02190810.1063/1.2162862 ↗
9. Luo C. H. · J. Appl. Phys. · 1997 · 82 · 380810.1063/1.365743 ↗
10. Choi J. · ACS Appl. Mater. Interfaces · 2013 · 5 · 1274410.1021/am4041338 ↗
11. Baglin J. E. E. · Thin Solid Films · 1982 · 93 · 25510.1016/0040-6090(82)90130-4 ↗
12. Kim E.-H. · RTP 2005, IEEE Int. Conf. Adv. Therm. Process. Semicond., 13th · 2005 · 177
13. Baglin J. E. · Appl. Phys. Lett. · 1980 · 36 · 59410.1063/1.91559 ↗
14. Ratajczak J. · J. Microsc. · 2010 · 237 · 37910.1111/j.1365-2818.2009.03264.x ↗
15. Nishimura T. · Appl. Phys. Lett. · 2007 · 91 · 12312310.1063/1.2789701 ↗
16. Huang W. · Appl. Surf. Sci. · 2008 · 254 · 212010.1016/j.apsusc.2007.08.081 ↗
17. Moulder J. F. · 1995
18. Cao Y. · Surf. Interface Anal. · 2009 · 41 · 47110.1002/sia.3050 ↗
19. Allred A. L. · J. Inorg. Nucl. Chem. · 1961 · 17 · 21510.1016/0022-1902(61)80142-5 ↗