Thermal Characterization of Ferroelectric Al1–xBxN for Nonvolatile Memory

Kyuhwe Kang, Joseph A. Casamento, Daniel C. Shoemaker, Yiwen Song, Erdem Z. Ozdemir, Nathaniel S. McIlwaine, Jon-Paul Maria, Sukwon Choi, Susan E. Trolier-McKinstry

ACS Applied Materials & Interfaces· Volume 16· Issue 49
Publisher page

Abstract

Boron (B)-substituted wurtzite AlN (Al 1– x B x N) is a recently discovered wurtzite ferroelectric material that offers several advantages over ferroelectric Hf 1– x Zr x O 2 and PbZr 1– x Ti x O 3 . Such benefits include a relatively low growth temperature as well as a thermally stable, and thickness-stable ferroelectric polarization; these factors are promising for the development of ferroelectric nonvolatile random-access memory (FeRAM) that are CMOS-compatible, scalable, and reliable for storing data in harsh environments. However, wurtzite ferroelectric materials may undergo exacerbated self-heating upon polarization switching relative to other ferroelectric materials; the larger energy loss is anticipated due to the higher coercive field and remanent polarization. This work provides insight into the polarization switching-induced self-heating of future FeRAM based on Al 1– x B x N. It was experimentally observed that the thermal conductivity of Al 1– x B x N thin films drops from 40.9 W m –1 K –1 to 4.35 W m –1 K –1 (which is 2 orders of magnitude lower than that of bulk AlN) when the B composition ( x ) increases from 0 to 0.18. The transient thermal response of an Al 0.93 B 0.07 N metal–ferroelectric–metal (MFM) capacitor was investigated using micro-Raman thermometry and validated via device thermal modeling. Further simulation studies reveal that the large heat generation rate and the low thermal conductivity is predicted to induce an instantaneous temperature rise that may exceed 150 °C in a FeRAM device based on a 5 nm thick Al 1– x B x N film at GHz frequency switching. In addition, thermal crosstalk within a FeRAM cell array exacerbates the self-heating, resulting in a predicted steady-state temperature rise that is an order of magnitude higher than that of a single bit-cell.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Acoustic Wave Resonator Technologies · Ferroelectric and Piezoelectric Materials · Metal and Thin Film Mechanics

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Mechanical Engineering, The Pennsylvania State University, University Park, Pennsylvania 16802, United States

Department of Materials Science and Engineering, The Pennsylvania State University, University Park, Pennsylvania 16802, United States

Funding

Army Research Office · National Science Foundation

References (69)

Show source-provided references
1. 10.1038/s41566-019-0359-910.1038/s41566-019-0359-9 ↗
2. 10.1002/aelm.20160050110.1002/aelm.201600501 ↗
3. 10.1002/adma.20080261110.1002/adma.200802611 ↗
4. 10.1557/mrs.2012.26810.1557/mrs.2012.268 ↗
5. 10.1063/1.508494510.1063/1.5084945 ↗
6. 10.1063/5.005786910.1063/5.0057869 ↗
7. 10.1063/5.018506610.1063/5.0185066 ↗
8. 10.1126/science.adh767010.1126/science.adh7670 ↗
9. 10.1088/1361-6641/acb80e10.1088/1361-6641/acb80e ↗
10. Fenouillet-Beranger, C.; Mathieu, B.; Previtali, B.; Samson, M.P.; Rambal, N.; Benevent, V.; Kerdiles, S. New Insights on Bottom Layer Thermal Stability and Laser Annealing Promises for High Performance 3D VLSI. In 2014 IEEE International Electron Devices Meeting; San Francisco, 2014, pp 27.5.1–27.5.4.10.1109/IEDM.2014.7047121 ↗
11. Cavalcante, C.; Fenouillet-Beranger, C.; Batude, P.; Garros, X.; Federspiel, X.; Lacord, J. 28nm FDSOI CMOS Technology (FEOL and BEOL) Thermal stability for 3D Sequential Integration: Yield and Reliability Analysis. In 2020; IEEE Symposium on VLSI Technology; Honolulu, 2020, pp 1–2.10.1109/VLSITechnology18217.2020.9265075 ↗
12. 10.1063/5.015282110.1063/5.0152821 ↗
13. 10.1063/5.005364910.1063/5.0053649 ↗
14. Rubat du Merac M. · 2021 · 1 · 399
15. 10.1103/PhysRevB.74.10411610.1103/PhysRevB.74.104116 ↗
16. 10.1103/PhysRevB.89.06410910.1103/PhysRevB.89.064109 ↗
17. Fichtner, S.; Schönweger, G.; Dietz, F.; Hanssen, H.; Züge, H.; Kreutzer, T. N.; Lofink, F.; Kohlstedt, H.; Kapels, H.; Mensing, M. Wurtzite-Type Ferroelectrics for Microelectronic Devices: Scalability and Integration to Silicon Based Ferroelectric FETs. 2023 7th IEEE Electron Devices Technology & Manufacturing Conference (EDTM); Institute of Electrical and Electronics Engineers Inc.: Seoul, 2023, pp 1–3.10.1109/EDTM55494.2023.10103080 ↗
18. 10.1063/5.003761710.1063/5.0037617 ↗
19. 10.1038/s41565-023-01361-y10.1038/s41565-023-01361-y ↗
20. 10.1038/s41928-024-01148-610.1038/s41928-024-01148-6 ↗
21. 10.1109/TNS.2010.208410110.1109/TNS.2010.2084101 ↗
22. 10.1007/s10853-005-7201-010.1007/s10853-005-7201-0 ↗
23. 10.1063/5.002958210.1063/5.0029582 ↗
24. 10.1063/5.011467010.1063/5.0114670 ↗
25. 10.1063/1.369088810.1063/1.3690888 ↗
26. 10.1063/1.480225010.1063/1.4802250 ↗
27. 10.1364/OPTICA.5.00127910.1364/OPTICA.5.001279 ↗
28. 10.1109/JMEMS.2019.291387510.1109/JMEMS.2019.2913875 ↗
29. 10.1002/aelm.20210093110.1002/aelm.202100931 ↗
30. 10.1111/j.1151-2916.1996.tb08095.x10.1111/j.1151-2916.1996.tb08095.x ↗
31. 10.1109/TDMR.2004.83721010.1109/TDMR.2004.837210 ↗
32. 10.1111/jace.1954010.1111/jace.19540 ↗
33. 10.1103/PhysRevMaterials.5.04441210.1103/PhysRevMaterials.5.044412 ↗
34. 10.1021/acsami.1c0291210.1021/acsami.1c02912 ↗
35. 10.1103/PhysRev.113.104610.1103/PhysRev.113.1046 ↗
36. 10.1016/0022-3697(87)90153-310.1016/0022-3697(87)90153-3 ↗
37. 10.1103/PhysRevB.66.19530410.1103/PhysRevB.66.195304 ↗
38. 10.1103/PhysRevMaterials.6.10460210.1103/PhysRevMaterials.6.104602 ↗
39. 10.1109/JEDS.2021.312927910.1109/JEDS.2021.3129279 ↗
40. Francois, T.; Grenouillet, L.; Coignus, J. Demonstration of BEOL-Compatible Ferroelectric Hf0.5Zr0.5O2 FeRAM Co-Integrated with 130nm CMOS for Embedded NVM Applications. 2019 IEEE International Electron Devices Meeting (IEDM); IEEE, 2019, pp 362–365.10.1109/IEDM19573.2019.8993485 ↗
41. 10.1063/1.164491710.1063/1.1644917 ↗
42. 10.1002/aelm.20220114210.1002/aelm.202201142 ↗
43. 10.1080/1058458950801290610.1080/10584589508012906 ↗
44. 10.1063/1.498371210.1063/1.4983712 ↗
45. 10.1080/1058458960801305010.1080/10584589608013050 ↗
46. 10.1002/adfm.20221394310.1002/adfm.202213943 ↗
47. Tran, Q.; Hayden, J.; Casamento, J.; Maria, J.P.; Jackosn, T. N. Boron-Doped Aluminum Nitride Ferroelectric Field-Effect Transistors with ZnO Semiconductor Channel. 2024 device research conference (DRC); Nature Research, 2024; Vol. 18.10.1109/DRC61706.2024.10605410 ↗
48. 10.1016/j.actamat.2024.11967810.1016/j.actamat.2024.119678 ↗
49. 10.1063/5.005627110.1063/5.0056271 ↗
50. 10.1063/1.181943110.1063/1.1819431 ↗
51. 10.1063/1.345715110.1063/1.3457151 ↗
52. 10.1016/j.cirpj.2017.09.00710.1016/j.cirpj.2017.09.007 ↗
53. 10.1088/0253-6102/48/5/03410.1088/0253-6102/48/5/034 ↗
54. 10.1103/PhysRevB.57.1055010.1103/PhysRevB.57.10550 ↗
55. Dobrovinskaya E. R. · 2009 · 5510.1007/978-0-387-85695-7_2 ↗
56. Cook J. G. · 2013 · 65
57. 10.1063/1.500679610.1063/1.5006796 ↗
58. 10.1115/1.404710010.1115/1.4047100 ↗
59. 10.1103/PhysRevB.56.740410.1103/PhysRevB.56.7404 ↗
60. 10.1103/PhysRevB.62.502810.1103/PhysRevB.62.5028 ↗
61. 10.1088/0370-1298/68/12/30310.1088/0370-1298/68/12/303 ↗
62. 10.1039/b801115j10.1039/b801115j ↗
63. 10.1021/acsami.0c0397810.1021/acsami.0c03978 ↗
64. 10.1063/5.000891910.1063/5.0008919 ↗
65. 10.1063/5.010691610.1063/5.0106916 ↗
66. 10.1016/j.carbon.2018.06.02510.1016/j.carbon.2018.06.025 ↗
67. 10.1103/PhysRevMaterials.3.08460710.1103/PhysRevMaterials.3.084607 ↗
68. 10.1109/TED.2023.330312510.1109/TED.2023.3303125 ↗
69. 10.1063/5.016409510.1063/5.0164095 ↗