Interface Passivation and Trap Reduction via a Solution-Based Method for Near-Zero Hysteresis Nanowire Field-Effect Transistors

In this letter, we demonstrate a solution-based method for a one-step deposition and surface passivation of the as-grown silicon nanowires (Si NWs). Using N,N-dimethylformamide (DMF) as a mild oxidizing agent, the NWs' surface traps density was reduced by over 2 orders of magnitude from 1×10(13) cm(-2) in pristine NWs to 3.7×10(10) cm(-2) in DMF-treated NWs, leading to a dramatic hysteresis reduction in NW field-effect transistors (FETs) from up to 32 V to a near-zero hysteresis. The change of the polyphenylsilane NW shell stoichiometric composition was confirmed by X-ray photoelectron spectroscopy analysis showing a 35% increase in fully oxidized Si4+ species for DMF-treated NWs compared to dry NW powder. Additionally, a shell oxidation effect induced by DMF resulted is a more stable NW FET performance with steady transistor currents and only 1.5 V hysteresis after 1000 h of air exposure.