Atomic-Scale Interface Modification Improves the Performance of Cu(In1–xGax)Se2/Zn(O,S) Heterojunction Solar Cells
Source abstract
Abstract
Cadmium-free buffer layers deposited by a dry vacuum process are mandatory for low-cost and environmentally friendly Cu(In1–xGax)Se2 (CIGS) photovoltaic in-line production. Zn(O,S) has been identified as an alternative to the chemical bath deposited CdS buffer layer, providing comparable power conversion efficiencies. Recently, a significant efficiency enhancement has been reported for sputtered Zn(O,S) buffers after an annealing treatment of the complete solar cell stack; the enhancement was attributed to interdiffusion at the CIGS/Zn(O,S) interface, resulting in wide-gap ZnSO4 islands formation and reduced interface defects. Here, we exclude interdiffusion or island formation at the absorber/buffer interface after annealing up to 200 °C using high-resolution scanning transmission electron microscopy (HR-STEM) and energy-dispersive X-ray spectroscopy (EDX). Interestingly, HR-STEM imaging reveals an epitaxial relationship between a part of the Zn(O,S) buffer layer grains and the CIGS grains induced by annealing at such a low temperature. This alteration of the CIGS/buffer interface is expected to lead to a lower density of interface defects, and could explain the efficiency enhancement observed upon annealing the solar cell stack, although other causes cannot be excluded.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Chalcogenide Semiconductor Thin Films · Quantum Dots Synthesis And Properties · Copper-based nanomaterials and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
International Iberian Nanotechnology Laboratory, Avenida Mestre José Veiga s/n, Braga 4715-330, Portugal
Università degli Studi di Genova, via Dodecaneso 31, Genova 16146, Italy
Universidade Politécnica de Madrid, Avenida Complutense 30, 28040 Madrid, Spain
NICE Solar Energy GmbH, 74523 Schwäbisch Hall, Germany
Funding
H2020 Marie Sk??odowska-Curie Actions
References (26)
Show source-provided references
1. 10.1063/1.152157710.1063/1.1521577 ↗
2. 10.1063/1.160051010.1063/1.1600510 ↗
3. 10.1063/1.192319410.1063/1.1923194 ↗
4. 10.1109/JPHOTOV.2014.229809310.1109/JPHOTOV.2014.2298093 ↗
5. 10.1063/1.475401410.1063/1.4754014 ↗
6. 10.1063/1.182505310.1063/1.1825053 ↗
7. 10.1063/1.222206710.1063/1.2222067 ↗
8. 10.1143/JJAP.50.04DP1010.1143/JJAP.50.04DP10 ↗
9. 10.1021/acsami.5b0481510.1021/acsami.5b04815 ↗
10. 10.1002/pssa.20143123210.1002/pssa.201431232 ↗
11. 10.1002/pip.244510.1002/pip.2445 ↗
12. 10.1002/pssr.20190014510.1002/pssr.201900145 ↗
13. 10.1063/1.490397610.1063/1.4903976 ↗
14. 10.1038/s41467-020-17434-810.1038/s41467-020-17434-8 ↗
15. 10.1016/j.solener.2020.01.07310.1016/j.solener.2020.01.073 ↗
16. 10.1016/j.solmat.2017.02.03110.1016/j.solmat.2017.02.031 ↗
17. 10.1016/j.tsf.2012.10.04010.1016/j.tsf.2012.10.040 ↗
18. 10.1021/acs.jpclett.6b0257710.1021/acs.jpclett.6b02577 ↗
19. 10.1021/jp804026v10.1021/jp804026v ↗
20. 10.1016/j.nantod.2017.12.01110.1016/j.nantod.2017.12.011 ↗
21. 10.1103/PhysRevB.64.24130410.1103/PhysRevB.64.241304 ↗
22. 10.1063/1.478871710.1063/1.4788717 ↗
23. 10.1016/j.actamat.2020.09.02810.1016/j.actamat.2020.09.028 ↗
24. 10.1016/j.solmat.2013.09.03010.1016/j.solmat.2013.09.030 ↗
25. 10.1016/S0040-6090(99)00768-310.1016/S0040-6090(99)00768-3 ↗
26. 10.1103/PhysRevMaterials.3.05460210.1103/PhysRevMaterials.3.054602 ↗