High-Performance Electron Field Emitters and Microplasma Cathodes Based on Conductive Hybrid Granular Structured Diamond Materials

High-performance diamond electron field emitters (EFEs) with extremely low turn-on field ( E 0 = 1.72 V/μm) and high current density (1.70 mA/cm 2 at an applied field of 3.86 V/μm) were successfully synthesized by using a modified two-step microwave plasma chemical deposition process. Such emitters possess EFE properties comparable with most of carbon- or semiconductor-based EFE materials, but with markedly better lifetime stability. The superb EFE behavior of these materials was achieved owing to the reduction in the diamond-to-Si interfacial resistance and the increase in the conductivity of the bulk diamond films (HBD –400 V ) via the applications of high bias voltage during the preparation of the ultrananocrystalline diamond (UNCD) primary layer and the subsequent plasma post-treatment (PPT) process, respectively. The superior EFE properties along with enhanced robustness of HBD –400 V films compared with the existing diamond-based EFE materials rendered these materials of greater potential for applications in high brightness display and multifunctional microplasma.