Brush Printing Creates Polarized Green Fluorescence: 3D Orientation Mapping and Stochastic Analysis of Conductive Polymer Films

Toshiki Sakata, Daisuke Kajiya, Ken-ichi Saitow

ACS Applied Materials & Interfaces· Volume 12· Issue 41
Publisher page

Abstract

Brush printing is a unique method used to obtain uniaxially oriented films, whereby a polymer solution is brushed onto a substrate. However, there have been only a few reports on the brush-printing method. Here, we report the preparation of a uniaxially oriented film of a green light-emitting conductive polymer, poly(9,9-dioctylfluorene-alt-benzothiadiazole) (F8BT). The fluorescence polarization ratio of the oriented F8BT films was as high as 11.3, and the average orientation factor reached 0.74 ± 0.06. The orientation factor and the torsion angle of F8BT were visualized by two mappings of fluorescence and Raman spectral measurements by confocal spectromicroscopy, respectively. These two x-y mapping data with many pixels (∼750 pixels) were evaluated by x-y-z mapping of the film thickness at a single position and were used to reveal the three-dimensional (3D) orientation mechanism from a stochastic approach. Polarized green fluorescence originates from polymer chains uniaxially oriented along the brush direction. The high orientation for a film thickness < 100 nm is established by shear stress, faster capillary flow, and flow-induced chain extension for a thin solution film on a substrate. The high orientation factor was also demonstrated by a high brushing speed, whereas an optimized brushing speed existed. We found that this optimization is attributed to the property of a non-Newtonian fluid. By applying this brush-printing method to the fabrication of an optoelectrical device, polarized green electroluminescence was preliminarily demonstrated by the OLED assembled from an oriented F8BT film.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Organic Light-Emitting Diodes Research · Organic Electronics and Photovoltaics · Nanomaterials and Printing Technologies

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Natural Science Center for Basic Research and Development (N-BARD), Hiroshima University, 1-3-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8526, Japan

Graduate School of Advanced Science and Engineering, Hiroshima University, 1-3-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8526, Japan

Funding

Precursory Research for Embryonic Science and Technology · Japan Society for the Promotion of Science · JKA Foundation

References (72)

Show source-provided references
1. 10.1002/adma.20130224010.1002/adma.201302240 ↗
2. 10.1021/jacs.0c0188310.1021/jacs.0c01883 ↗
3. 10.1039/C4EE00688G10.1039/C4EE00688G ↗
4. 10.1021/am200705j10.1021/am200705j ↗
5. 10.1021/cm049473l10.1021/cm049473l ↗
6. 10.1021/am509047g10.1021/am509047g ↗
7. 10.1038/natrevmats.2018.2010.1038/natrevmats.2018.20 ↗
8. 10.1039/C8TA09383K10.1039/C8TA09383K ↗
9. 10.1016/j.jphotochem.2010.04.01510.1016/j.jphotochem.2010.04.015 ↗
10. 10.1021/jz400723u10.1021/jz400723u ↗
11. 10.1021/acs.jpcc.6b0710110.1021/acs.jpcc.6b07101 ↗
12. 10.1021/acs.jpcc.9b0514410.1021/acs.jpcc.9b05144 ↗
13. 10.1021/ma500762x10.1021/ma500762x ↗
14. 10.1063/1.11490010.1063/1.114900 ↗
15. 10.1021/jz300710a10.1021/jz300710a ↗
16. 10.1002/adfm.20110113910.1002/adfm.201101139 ↗
17. 10.1021/jp510675r10.1021/jp510675r ↗
18. 10.1021/acs.jpcc.6b0683310.1021/acs.jpcc.6b06833 ↗
19. 10.1021/ma102137v10.1021/ma102137v ↗
20. 10.1021/ma025887t10.1021/ma025887t ↗
21. 10.1063/1.471842410.1063/1.4718424 ↗
22. 10.1021/ma049051x10.1021/ma049051x ↗
23. 10.1063/1.214208210.1063/1.2142082 ↗
24. 10.1002/macp.20160017810.1002/macp.201600178 ↗
25. 10.1002/adfm.20110090410.1002/adfm.201100904 ↗
26. 10.1002/adfm.20130335110.1002/adfm.201303351 ↗
27. 10.1021/acsami.5b0871010.1021/acsami.5b08710 ↗
28. 10.1038/s41598-017-05396-910.1038/s41598-017-05396-9 ↗
29. 10.1021/acs.macromol.5b0164710.1021/acs.macromol.5b01647 ↗
30. 10.1039/C3TC32056A10.1039/C3TC32056A ↗
31. 10.1063/1.299954110.1063/1.2999541 ↗
32. 10.1021/nn800574f10.1021/nn800574f ↗
33. 10.1038/ncomms1607010.1038/ncomms16070 ↗
34. 10.1038/ncomms939410.1038/ncomms9394 ↗
35. 10.1021/acsami.8b0711810.1021/acsami.8b07118 ↗
36. 10.1021/acsami.7b0813310.1021/acsami.7b08133 ↗
37. 10.1021/acsami.6b0160710.1021/acsami.6b01607 ↗
38. 10.1126/sciadv.aaw775710.1126/sciadv.aaw7757 ↗
39. 10.1021/nl070022k10.1021/nl070022k ↗
40. 10.1039/C5CC05247E10.1039/C5CC05247E ↗
41. 10.1039/C6CC05522B10.1039/C6CC05522B ↗
42. 10.1021/acs.langmuir.9b0040210.1021/acs.langmuir.9b00402 ↗
43. 10.1002/adma.20160698710.1002/adma.201606987 ↗
44. 10.1073/pnas.171363411410.1073/pnas.1713634114 ↗
45. 10.1021/am301732m10.1021/am301732m ↗
46. 10.1021/acsami.6b0672310.1021/acsami.6b06723 ↗
47. 10.1021/jacs.5b0188910.1021/jacs.5b01889 ↗
48. 10.1021/am503786210.1021/am5037862 ↗
49. 10.1002/adma.20110351310.1002/adma.201103513 ↗
50. 10.1002/adma.20110460210.1002/adma.201104602 ↗
51. 10.1021/cm049585c10.1021/cm049585c ↗
52. 10.1021/jp809589n10.1021/jp809589n ↗
53. 10.1021/am201027j10.1021/am201027j ↗
54. 10.1063/1.492141510.1063/1.4921415 ↗
55. 10.1039/C5NR02361K10.1039/C5NR02361K ↗
56. 10.1063/1.493913510.1063/1.4939135 ↗
57. 10.1021/acsaem.8b0126010.1021/acsaem.8b01260 ↗
58. 10.1039/C8NR05650A10.1039/C8NR05650A ↗
59. 10.1021/acsaelm.9b0067310.1021/acsaelm.9b00673 ↗
60. 10.1103/PhysRevB.77.11533810.1103/PhysRevB.77.115338 ↗
61. In general, orientation factor, Sa (=R−1R+1), obtained from absorption spectra can range from +1 to −1, where +1 and −1 correspond to R (=A∥A⊥) = ∞ and 0, respectively. The former and latter situations are established as A⊥ = 0 and A∥ = 0, respectively. Here, the fluorescence polarization was treated as the orientation factor Sf (=I∥−I⊥I∥+I⊥). In general, Sf can also range from +1 to −1. The former and latter situations are established as I⊥ = 0 and I∥ = 0, respectively, whose situation is the same as the orientation factor of Sa.
62. To consider the alignment of polymer molecules that do not involve crystalline aggregates of F8BT, Sf was evaluated from the fluorescence spectra using a shorter wavelength (500–525 nm). This is because the component of the fluorescence spectra in a longer wavelength has been characterized as a component of crystalline aggregates for π-conjugated polymers in refs.(63,64) In fact, fluorene polymers show red-shifted PL by forming aggregates, e.g., refs.(65,66) The fluorescence spectra of F8BT have spectral components at longer wavelengths, which might be due to aggregate species. However, the species of longer wavelength have not been attributed to date, to the best of our knowledge.
63. 10.1038/nmat372210.1038/nmat3722 ↗
64. 10.1021/acs.jpclett.6b0164110.1021/acs.jpclett.6b01641 ↗
65. 10.1002/(SICI)1521-4044(199808)49:8<439::AID-APOL439>3.0.CO;2-A10.1002/(SICI)1521-4044(199808)49:8<439::AID-APOL439>3.0.CO;2-A ↗
66. 10.1002/cphc.20200011810.1002/cphc.202000118 ↗
67. 10.1021/ja051891j10.1021/ja051891j ↗
68. Çengel, Y. A.; Cimbala, J. M. Fluid Mechanics: Fundamentals and Applications, Second Edition; McGraw-Hill Higher Education: New York, 2010, pp. 51–52.
69. 10.1021/jp011832210.1021/jp0118322 ↗
70. 10.1038/nature1034410.1038/nature10344 ↗
71. 10.1021/la047528s10.1021/la047528s ↗
72. 10.1016/0095-8522(65)90022-X10.1016/0095-8522(65)90022-X ↗