Recombination Suppression in PbS Quantum Dot Heterojunction Solar Cells by Energy-Level Alignment in the Quantum Dot Active Layers

Chao Ding, Yaohong Zhang, Feng Liu, Naoki Nakazawa, Qingxun Huang, Shuzi Hayase, Yuhei Ogomi, Taro Toyoda, Ruixiang Wang, Qing Shen

ACS Applied Materials & Interfaces· Volume 10· Issue 31

Abstract

Using spatial energy-level gradient engineering with quantum dots (QDs) of different sizes to increase the generated carrier collection at the junction of a QD heterojunction solar cell (QDHSC) is a hopeful route for improving the energy-conversion efficiency. However, the results of current related research have shown that a variable band-gap structure in a QDHSC will create an appreciable increase, not in the illumination current density, but rather in the fill factor. In addition, there are a lack of studies on the mechanism of the effect of these graded structures on the photovoltaic performance of QDHSCs. This study presents the development of air atmosphere solution-processed TiO2/PbS QDs/Au QDHSCs by engineering the energy-level alignment (ELA) of the active layer via the use of a sorted order of differently sized QD layers (four QD sizes). In comparison to the ungraded device (without the ELA), the optimized graded architecture (containing the ELA) solar cells exhibited a great increase (21.4%) in short-circuit current density (Jsc). As a result, a Jsc value greater than 30 mA/cm2 has been realized in planar, thinner absorption layer (∼300 nm) PbS QDHSCs, and the open-circuit voltage (Voc) and power-conversion efficiency (PCE) were also improved. Through characterization by the light intensity dependences of the Jsc and Voc and transient photovoltage decay, we find that (i) the ELA structure, serving as an electron-blocking layer, reduces the interfacial recombination at the PbS/anode interface, and (ii) the ELA structure can drive more carriers toward the desirable collection electrode, and the additional carriers can fill the trap states, reducing the trap-assisted recombination in the PbS QDHSCs. This work has clearly elucidated the mechanism of the recombination suppression in the graded QDHSCs and demonstrated the effects of ELA structure on the improvement of Jsc. The charge recombination mechanisms characterized in this work would be able to shed light on further improvements of QDHSCs, which could even benefit other types of solar cells.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Quantum Dots Synthesis And Properties · Chalcogenide Semiconductor Thin Films · TiO2 Photocatalysis and Solar Cells

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Graduate School of Informatics and Engineering, The University of Electro-Communications, 1-5-1 Chofugaoka, Chofu, Tokyo 182-8585, Japan

China Scholarship Council, Level 13, Building A3, No.9 Chegongzhuang Avenue, Beijing 100044, China

Graduate School of Life Science and Systems Engineering, Kyushu Institute of Technology, 2-4 Hibikino, Wakamatsu-ku, Kitakyushu, Fukuoka 808-0196, Japan

CREST, Japan Science and Technology Agency (JST), 4-1-8 Honcho, Kawaguchi, Saitama 332-0012, Japan

Beijing Engineering Research Centre of Sustainable Energy and Buildings, Beijing University of Civil Engineering and Architecture, No.15 Yongyuan Road, Huangcun, Daxing, Beijing 102616, China

Funding

Ministry of Education, Culture, Sports, Science and Technology · Core Research for Evolutional Science and Technology · Japan Science and Technology Agency · China Scholarship Council

References (45)

Show source-provided references
1. 10.1021/ja003633m10.1021/ja003633m ↗
2. 10.1021/nn100335g10.1021/nn100335g ↗
3. 10.1021/ar800112v10.1021/ar800112v ↗
4. 10.1021/ar970220q10.1021/ar970220q ↗
5. 10.1021/la971386310.1021/la9713863 ↗
6. 10.1038/nmat398410.1038/nmat3984 ↗
7. 10.1002/adma.20150365710.1002/adma.201503657 ↗
8. 10.1021/acs.nanolett.5b0367710.1021/acs.nanolett.5b03677 ↗
9. 10.1021/acs.nanolett.6b0195710.1021/acs.nanolett.6b01957 ↗
10. 10.1021/acs.nanolett.6b0524110.1021/acs.nanolett.6b05241 ↗
11. 10.1063/1.481307410.1063/1.4813074 ↗
12. 10.1002/adma.20120294210.1002/adma.201202942 ↗
13. 10.1021/nl201682h10.1021/nl201682h ↗
14. 10.1016/j.solmat.2015.06.00710.1016/j.solmat.2015.06.007 ↗
15. 10.1039/C5RA10715F10.1039/C5RA10715F ↗
16. 10.1038/ncomms877210.1038/ncomms8772 ↗
17. 10.1002/adma.20120450210.1002/adma.201204502 ↗
18. 10.1021/acs.jpcc.5b0034110.1021/acs.jpcc.5b00341 ↗
19. 10.1063/1.9555310.1063/1.95553 ↗
20. 10.1063/1.32208310.1063/1.322083 ↗
21. 10.1016/S0927-0248(00)00274-910.1016/S0927-0248(00)00274-9 ↗
22. Nelson J. · 2003 · 28910.1142/9781848161269_0010 ↗
23. 10.1038/nmat311810.1038/nmat3118 ↗
24. 10.1021/nn900863a10.1021/nn900863a ↗
25. 10.1021/acsnano.5b0683310.1021/acsnano.5b06833 ↗
26. 10.1063/1.173603410.1063/1.1736034 ↗
27. 10.1039/C4NR07521H10.1039/C4NR07521H ↗
28. 10.1002/adma.20170074910.1002/adma.201700749 ↗
29. 10.1002/adfm.20090110710.1002/adfm.200901107 ↗
30. 10.1021/acsnano.5b0032110.1021/acsnano.5b00321 ↗
31. 10.1021/nn400656n10.1021/nn400656n ↗
32. 10.1021/nn501185h10.1021/nn501185h ↗
33. 10.1002/adfm.20030439910.1002/adfm.200304399 ↗
34. 10.1038/srep1062610.1038/srep10626 ↗
35. 10.1103/PhysRevB.82.24520710.1103/PhysRevB.82.245207 ↗
36. 10.1002/aenm.20120108310.1002/aenm.201201083 ↗
37. 10.1021/acs.jpcc.6b1092010.1021/acs.jpcc.6b10920 ↗
38. 10.1021/acs.jpclett.7b0068310.1021/acs.jpclett.7b00683 ↗
39. 10.1016/0379-6787(88)90084-110.1016/0379-6787(88)90084-1 ↗
40. 10.1002/cphc.20020061510.1002/cphc.200200615 ↗
41. 10.1016/j.egypro.2013.07.07110.1016/j.egypro.2013.07.071 ↗
42. 10.1016/j.solener.2009.04.00410.1016/j.solener.2009.04.004 ↗
43. 10.1021/nn402197a10.1021/nn402197a ↗
44. 10.1021/ja400948t10.1021/ja400948t ↗
45. 10.1021/acsami.5b0178910.1021/acsami.5b01789 ↗