Coherent Random Lasing from Dye Aggregates in Polydimethylsiloxane Thin Films

The coherent random laser (CRL) from dye-doped polydimethylsiloxane (PDMS) has been investigated in both nanoparticle-doped (NP-doped) thin films and pure dye thin films. Compared with the literature, the pump threshold is only 1.5 mJ/cm 2 in the pure dye thin film with a low dye concentration. The spontaneously formed micro-/nanocrystals of Pyrromethene 597 (PM597) dye support both gain and random feedback in the bulk of the PDMS during the sample preparation. When the SiO 2 NPs were doped, the pump threshold was reduced to 0.75 mJ/cm 2 . The threshold increased after the film was peeled off from glass, which indicates that the photon localization effect of the leaky-waveguide structure plays an important role in the reduction of the CRL threshold. By a change in the pump stripe length or the thickness of the film, the peak wavelength red-shifts 6.7 or 5.93 nm, respectively. The PM597 dye molecule solubility changes, and they spontaneously aggregate in the process of toluene volatilization; the PDMS cures, which is the reason for the formation of PM597 micro-/nanocrystals. This thin film random laser with a low dye concentration can be used in integrated optoelectronics and display imaging.