Atomic Layer Deposition of Electron Selective SnOx and ZnO Films on Mixed Halide Perovskite: Compatibility and Performance
Source abstract
Abstract
The compatibility of atomic layer deposition directly onto the mixed halide perovskite formamidinium lead iodide:methylammonium lead bromide (CH(NH 2 ) 2, CH 3 NH 3 )Pb(I,Br) 3 (FAPbI 3:MAPbBr 3 ) perovskite films is investigated by exposing the perovskite films to the full or partial atomic layer deposition processes for the electron selective layer candidates ZnO and SnO x . Exposing the samples to the heat, the vacuum, and even the counter reactant of H 2 O of the atomic layer deposition processes does not appear to alter the perovskite films in terms of crystallinity, but the choice of metal precursor is found to be critical. The Zn precursor Zn(C 2 H 5 ) 2 either by itself or in combination with H 2 O during the ZnO atomic layer deposition (ALD) process is found to enhance the decomposition of the bulk of the perovskite film into PbI 2 without even forming ZnO. In contrast, the Sn precursor Sn(N(CH 3 ) 2 ) 4 does not seem to degrade the bulk of the perovskite film, and conformal SnO x films can successfully be grown on top of it using atomic layer deposition. Using this SnO x film as the electron selective layer in inverted perovskite solar cells results in a lower power conversion efficiency of 3.4% than the 8.4% for the reference devices using phenyl-C 70 -butyric acid methyl ester. However, the devices with SnO x show strong hysteresis and can be pushed to an efficiency of 7.8% after biasing treatments. Still, these cells lacks both open circuit voltage and fill factor compared to the references, especially when thicker SnO x films are used. Upon further investigation, a possible cause of these losses could be that the perovskite/SnO x interface is not ideal and more specifically found to be rich in Sn, O, and halides, which is probably a result of the nucleation during the SnO x growth and which might introduce barriers or alter the band alignment for the transport of charge carriers.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Perovskite Materials and Applications · Quantum Dots Synthesis And Properties · Chalcogenide Semiconductor Thin Films
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Solid State Electronics, Department of Engineering Sciences, Uppsala University, 751 21 Uppsala, Sweden
Physical Chemistry, Department of Chemistry - Ångström Laboratory, Uppsala University, 751 20 Uppsala, Sweden
Department of Physics, Sharif University of Technology, 145 88 Tehran, Iran
Funding
Energimyndigheten · Stiftelsen f?r?Strategisk Forskning · Seventh Framework Programme · STandUP for Energy · Stiftelsen Marcus och Amalia Wallenbergs Minnesfond
References (39)
Show source-provided references
1. 10.1039/C5EE03874J10.1039/C5EE03874J ↗
2. 10.1126/science.122860410.1126/science.1228604 ↗
3. 10.1038/srep0059110.1038/srep00591 ↗
4. 10.1039/C7TA00366H10.1039/C7TA00366H ↗
5. 10.1039/C5TA09011C10.1039/C5TA09011C ↗
6. 10.1039/C5EE02733K10.1039/C5EE02733K ↗
7. 10.1021/cr900056b10.1021/cr900056b ↗
8. 10.1039/C5TA07186K10.1039/C5TA07186K ↗
9. 10.1039/C4TA06128D10.1039/C4TA06128D ↗
10. 10.1039/C6EE02687G10.1039/C6EE02687G ↗
11. 10.1039/C6SE00076B10.1039/C6SE00076B ↗
12. 10.1038/nature1413310.1038/nature14133 ↗
13. Zimmermann, U.; Ruth, M.; Edoff, M.Cadmium-Free CIGS Mini-Modules with ALD-Grown Zn(O, S)-Based Buffer Layers. In21st European Photovoltaic Solar Energy Conference: Proceedings of the International Conference, Dresden, Germany, 4–8 September 2006;WIP-Renewable Energies:Munich, 2006; pp1831–1834.
14. 10.1002/pip.115310.1002/pip.1153 ↗
15. 10.1039/C5EE00120J10.1039/C5EE00120J ↗
16. 10.1109/JPHOTOV.2013.225623210.1109/JPHOTOV.2013.2256232 ↗
17. 10.1039/C5RA27424A10.1039/C5RA27424A ↗
18. 10.1021/acs.chemmater.5b0412210.1021/acs.chemmater.5b04122 ↗
19. 10.1021/jacs.6b0632010.1021/jacs.6b06320 ↗
20. 10.1021/cm504199710.1021/cm5041997 ↗
21. 10.1021/acs.chemmater.5b0034810.1021/acs.chemmater.5b00348 ↗
22. 10.1016/0368-2048(88)85018-710.1016/0368-2048(88)85018-7 ↗
23. 10.1039/C6CP06989D10.1039/C6CP06989D ↗
24. 10.1038/ncomms1033410.1038/ncomms10334 ↗
25. 10.1126/science.aaf971710.1126/science.aaf9717 ↗
26. 10.1039/C4EE03664F10.1039/C4EE03664F ↗
27. 10.1021/jacs.5b0076110.1021/jacs.5b00761 ↗
28. 10.1021/jz500113x10.1021/jz500113x ↗
29. 10.1039/C4EE02465F10.1039/C4EE02465F ↗
30. 10.1039/c2cp41394a10.1039/c2cp41394a ↗
31. 10.1039/C5EE02608C10.1039/C5EE02608C ↗
32. 10.1016/0039-6028(66)90083-510.1016/0039-6028(66)90083-5 ↗
33. 10.1016/S0022-0248(00)00731-410.1016/S0022-0248(00)00731-4 ↗
34. 10.1021/acs.jpcc.6b1185310.1021/acs.jpcc.6b11853 ↗
35. 10.1039/C6RA28501E10.1039/C6RA28501E ↗
36. 10.1002/adom.20170013910.1002/adom.201700139 ↗
37. 10.1002/aenm.20150096310.1002/aenm.201500963 ↗
38. 10.7567/JJAP.54.03230110.7567/JJAP.54.032301 ↗
39. 10.1038/nenergy.2017.910.1038/nenergy.2017.9 ↗