Alternative Synthesis of CuFeSe₂ Nanocrystals with Magnetic and Photoelectric Properties

Monodisperse CuFeSe2 nanocrystals of high quality have been successfully synthesized for the first time using a hot-solution injection method from the reaction of metallic acetylacetonates with diphenyl diselenide (Ph2Se2) in oleylamine with addition of oleic acid at 255 °C for 90 min. The characterizations of X-ray diffraction, electron microscopy, and compositional analysis reveal that the resulting CuFeSe2 nanocrystals are of tetragonal phase with a stoichiometric composition. The CuFeSe2 nanocrystals exhibit well-defined quasi-cubic shape with an average size of ∼18 nm, and their shape can be tuned from quasi-cubes to quasi-spheres by adjusting the reaction parameters. Magnetic measurement reveals that the as-synthesized CuFeSe2 nanocrystals are ferromagnetic and paramagnetic at 4 and 300 K, respectively. Additionally, the current-voltage (I-V) behavior of the CuFeSe2 nanocrystals suggests that they are promising candidates for application in optoelectronics and solar energy conversion.