Gallium Doping Effects for Improving Switching Performance of p-Type Copper(I) Oxide Thin-Film Transistors
Source abstract
Abstract
Copper(I) oxide (Cu2O), which is obtained from copper(II) oxide (CuO) through a reduction process, is a p-type oxide material with a band gap of 2.1-2.4 eV. However, the switching performance of typical Cu2O thin-film transistors (TFTs) is poor because the reduction process increases the concentration of oxygen vacancies (VO), which interfere with the conduction of hole carriers. Ga with high oxygen affinity was doped in Cu2O thin films to decrease VO during the reduction process. As a result, the VO concentration of 1.56 at % for Ga-doped Cu2O (Ga:Cu2O) thin films decreased from 20.2 to 7.5% compared to pristine Cu2O thin films. Accordingly, the subthreshold swing or S-factor, on/off-current ratio (Ion/off), saturation mobility (μsat), and threshold voltage (Vth) of Ga:Cu2O TFTs were improved compared to pristine Cu2O TFTs with values of 7.72 from 12.50 V/dec, 1.22 × 104 from 2.74 × 102, 0.74 from 0.46 cm2/Vs, and -4.56 from -8.06 V, respectively. These results indicate that Ga plays an important role in improving the switching performance of p-type Cu2O TFT.
Source: europepmc · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Thin-Film Transistor Technologies · ZnO doping and properties · Copper-based nanomaterials and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Electrical and Electronic Engineering, Yonsei University, 50 Yonsei-ro, Seodaemun-gu, Seoul 03722, Republic of Korea
Research and Development Center, LG Display, E2 Block LG Science Park, 30, Magokjungang 10-ro, Gangseo-gu, Seoul 07796, Republic of Korea
Funding
LG Display · Ministry of Science and ICT, South Korea · National Research Foundation of Korea
References (35)
Show source-provided references
1. 10.1038/nature0309010.1038/nature03090 ↗
2. 10.1063/1.311256610.1063/1.3112566 ↗
3. 10.1063/1.154267710.1063/1.1542677 ↗
4. 10.1038/nmat291410.1038/nmat2914 ↗
5. 10.1116/1.476411010.1116/1.4764110 ↗
6. 10.1063/1.296419710.1063/1.2964197 ↗
7. 10.1063/1.346993910.1063/1.3469939 ↗
8. 10.1039/c3cp50197c10.1039/c3cp50197c ↗
9. 10.1021/nn400852r10.1021/nn400852r ↗
10. 10.1038/s41524-018-0073-z10.1038/s41524-018-0073-z ↗
11. 10.1088/0953-8984/28/38/38300210.1088/0953-8984/28/38/383002 ↗
12. 10.3390/coatings902013710.3390/coatings9020137 ↗
13. 10.1002/adma.20150308010.1002/adma.201503080 ↗
14. 10.1038/4008710.1038/40087 ↗
15. 10.1103/PhysRevB.76.04520910.1103/PhysRevB.76.045209 ↗
16. 10.1103/PhysRevB.74.19512810.1103/PhysRevB.74.195128 ↗
17. 10.1116/1.349103610.1116/1.3491036 ↗
18. 10.1109/LED.2010.205057610.1109/LED.2010.2050576 ↗
19. 10.1016/j.ceramint.2015.12.10910.1016/j.ceramint.2015.12.109 ↗
20. 10.1063/1.133758710.1063/1.1337587 ↗
21. 10.1023/A:100995992043510.1023/A:1009959920435 ↗
22. 10.1039/C8TC06270F10.1039/C8TC06270F ↗
23. 10.1016/0254-0584(92)90243-210.1016/0254-0584(92)90243-2 ↗
24. 10.1111/j.1551-2916.2004.00683.x10.1111/j.1551-2916.2004.00683.x ↗
25. 10.1063/1.477168110.1063/1.4771681 ↗
26. 10.1002/ejic.20040025810.1002/ejic.200400258 ↗
27. 10.1039/c3ce26932a10.1039/c3ce26932a ↗
28. 10.1016/j.tsf.2017.09.05410.1016/j.tsf.2017.09.054 ↗
29. 10.1038/srep2186910.1038/srep21869 ↗
30. 10.1021/acsami.8b1237310.1021/acsami.8b12373 ↗
31. Kim J.-P. · J. Ceram. Process. Res. · 2012 · 13 · S96
32. 10.1103/PhysRevB.92.19530610.1103/PhysRevB.92.195306 ↗
33. 10.1021/jp205348p10.1021/jp205348p ↗
34. 10.1016/S0925-4005(98)00073-210.1016/S0925-4005(98)00073-2 ↗
35. 10.1103/PhysRevB.69.02410910.1103/PhysRevB.69.024109 ↗