Cation and Anion Co-doped Perovskite Nanofibers for Highly Efficient Electrocatalytic Oxygen Evolution

Perovskite oxides have been recognized as one of the most attractive oxygen evolution reaction (OER) catalysts because of their low cost, earth abundance, and robust nature. Herein, one-dimensional porous LaFe1–xNixO3 (LFNO) perovskite oxide nanofibers (LFNO NFs) are fabricated with a feasible electrospinning route and its further post-calcination treatment. By tailoring the atomic percent of Fe and Ni in the perovskite oxide, we determined that LaFe0.25Ni0.75O3 (LFNO-III) NFs afford the best OER activity among all the prepared perovskite oxides. Especially remarkable is that the further selenide-doped LaFe0.25Ni0.75O3 (LFNOSe-III) NFs exhibit outstanding OER activity with a low overpotential of 287 mV at 10 mA cm–2 and a small Tafel slope of 87 mV dec–1 in 1 M KOH solution, markedly exceeding that of the parent perovskite oxide and the commercial RuO2. It also delivers decent durability with no significant degradation after 22 h of stability test. In the meanwhile, density functional theory calculations are also conducted to justify the optimized adsorption features of *OH, *O, and *OOH intermediates and unveil that the electrocatalytic active sites are the Ni atoms adjacent to Fe in the Ni- and Se codoped perovskite. This work provides an effective method for the development of highly efficient perovskite oxide catalysts.