Improved sulfurization process for enhancing the microstructure and transport properties of spray pyrolysis-deposited Cu2ZnSnS4 films
Source abstract
Abstract
Cu 2 ZnSnS 4 (CZTS) is an emerging material with significant potential as an absorber layer for solar cells. Precise control over the film preparation process is crucial for attaining optimal transport, electrical, and optical properties. This study investigates the effect of sulfurization duration on the properties of CZTS films deposited onto soda lime glass substrates via spray pyrolysis, followed by annealing at 550 °C in a sulfur-rich environment under argon flow. X-ray diffraction and Raman spectroscopy confirmed the formation of monophasic CZTS, with the highest phase purity observed for films sulfurized for 5 minutes. Scanning electron microscopy demonstrated notable morphological and microstructural enhancements due to the sulfurization process, while energy-dispersive spectroscopy confirmed near-ideal stoichiometric composition (Cu:Zn:Sn:S ≈ 2:1:1:4). Optical spectroscopy determined the band gap of the films to be between 1.40 and 1.50 eV. The electrical transport properties were investigated up to 130 °C, revealing p-type conductivity, with Seebeck coefficients ranging from 30 to 70 μV K -2 and low electrical resistivity, displaying semiconductor-like behavior. The maximum power factor achieved was 0.36 μW mK -2 at 130 °C for the sample sulfurized for 5 minutes. These findings suggest that a 5-minute sulfurization time is optimal for producing single-phase CZTS films characterized by uniform morphology, accurate stoichiometric composition, and an ideal direct band gap. Given its favorable thermoelectric properties, CZTS shows significant promise as a material for thermoelectric applications, particularly in waste heat recovery systems. The results indicate that CZTS films could be further optimized for use in thermoelectric devices, and future studies could focus on enhancing their thermoelectric performance by adjusting sulfurization conditions and exploring material modifications.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Chalcogenide Semiconductor Thin Films · Quantum Dots Synthesis And Properties · Copper-based nanomaterials and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (67)
Show source-provided references
1. Secondary phase formation during monoclinic Cu2SnS3 growth for solar cell application10.1016/j.solmat.2016.04.039 ↗
2. Silver-substituted (Ag1-xCux)2ZnSnS4 solar cells from aprotic molecular inks10.1016/j.ceramint.2022.04.116 ↗
3. Engineering of interface band bending and defects elimination via a Ag-graded active layer for efficient (Cu,Ag)2ZnSn(S,Se)4 solar cells10.1039/C7EE01405H ↗
4. Cu2ZnSnS4 solar cells with over 10% power conversion efficiency enabled by heterojunction heat treatment10.1038/s41560-018-0206-0 ↗
5. Thermoelectric and photovoltaic properties of Mn-Doped kesterite Cu2Zn1–xMnxSnSe410.1021/acs.inorgchem.2c02403 ↗
6. Cu2ZnSnS4 films properties deposited by spray pyrolysis, subjected to a combined novel thermal treatment: CSS sulfurization and RTA post-treatment10.1016/j.jallcom.2023.170379 ↗
7. Anca Duta, effect of copper content and sulfurization process on optical, structural and electrical properties of ultrasonic spray pyrolysed Cu2ZnSnS410.1016/j.matchemphys.2015.11.035 ↗
8. Effect of sulfurization on the properties of Cu2ZnSnS4 thin films deposited using chemical spray pyrolysis over ITO substrates10.1016/j.solener.2017.08.051 ↗
9. 12.3% efficient low voc loss pure sulfide kesterite solar cells from DMSO solution via cadmium alloying10.1002/aenm.202301780 ↗
10. On the formation mechanisms of Zn-rich Cu2ZnSnS4 films prepared by sulfurization of metallic stacks10.1016/j.solmat.2013.01.015 ↗
11. Growth of Cu2ZnSnS4 (CZTS) thin films using short sulfurization periods10.1088/2053-1591/aaff78 ↗
12. Effects of element ratio on robustness of CZTS films: variations in sulfurization temperature10.1016/j.ceramint.2020.07.079 ↗
13. Investigation on the sulfurization temperature dependent phase and defect formation of sequentially evaporated Cu-rich CZTS thin films10.1016/j.solener.2020.03.007 ↗
14. X-ray resonant single-crystal diffraction technique, a powerful tool to investigate the kesterite structure of the photovoltaic Cu2ZnSnS4 compound10.1107/S2052520614003138 ↗
15. Enhancing the optoelectronic performance of CZTS thin films through cobalt doping via nebulizer-assisted spray pyrolysis technique10.1016/j.sna.2023.114941 ↗
16. The order-disorder transition in Cu2ZnSnS4 - a neutron scattering investigation10.1016/j.jssc.2016.03.013 ↗
17. Comprehensive investigation on ruthenium doped Sn2S3 thin films for photo sensing applications10.1016/j.physb.2024.416380 ↗
18. Effect of thermal annealing on nebulizer spray deposited tin sulfide thin films and their application in a transparent Oxide/cdS/SnS heterostructure10.1016/j.tsf.2018.09.014 ↗
19. Structural polymorphism in “Kesterite” Cu2ZnSnS4: raman spectroscopy and first-principles calculations analysis10.1021/acs.inorgchem.6b03008 ↗
20. Non-stoichiometry effect and disorder in Cu2ZnSnS4 thin films obtained by flash evaporation: raman scattering investigation10.1016/j.actamat.2013.11.010 ↗
21. Characterization of vibrational and mechanical properties of quaternary compounds Cu2ZnSnS4 and Cu2ZnSnSe4 in kesterite and stannite structures10.1103/PhysRevB.84.205201 ↗
22. Vibrational properties of stannite and kesterite type compounds: raman scattering analysis of Cu2(Fe,Zn)SnS410.1016/j.jallcom.2012.06.042 ↗
23. Development of a selective chemical Etch to improve the conversion efficiency of Zn-rich Cu2ZnSnS4 solar cells10.1021/ja301373e ↗
24. Raman mapping of MoS2 at Cu2ZnSnS4/Mo interface in thin film10.1016/j.solener.2020.05.043 ↗
25. Direct synthesis of single-phase p-type SnS by electrodeposition from a dicyanamide ionic liquid at high temperature for thin film solar cells10.1021/jp311552g ↗
26. ChemInform abstract: atmospheric pressure chemical vapor deposition of tin sulfides (SnS, Sn2S3, and SnS2) on glass
27. Anion distributions and phase transitions in CuS1-xSex(x = 0-1) studied by raman spectroscopy10.1006/jssc.1993.1242 ↗
28. Effect of annealing temperature on the properties of spray deposited Cu2SnS3 thin films
29. Characterization of Cu2SnS3 polymorphism and its impact on optoelectronic properties10.1039/C7TA08705E ↗
30. Effect of the stacking order, annealing temperature and atmosphere on crystal phase and optical properties of Cu2SnS310.1038/s41598-022-12045-3 ↗
31. Lattice vibrations in AIBIIIC2VI chalcopyrite compounds
32. Secondary phases and their influence on optical and electrical properties of electrodeposited Cu2FeSnS4 films10.1007/s00339-021-05038-y ↗
33. Raman scattering crystalline assessment of polycrystalline Cu2ZnSnS4 thin films for sustainable photovoltaic technologies: phonon confinement model10.1016/j.actamat.2014.02.035 ↗
34. Raman scattering and disorder effect in Cu2ZnSnS410.1002/pssr.201307073 ↗
35. Polarized Raman scattering study of kesterite type Cu2ZnSnS4 single crystals10.1038/srep19414 ↗
36. Multiwavelength excitation Raman scattering study of polycrystalline kesterite Cu2ZnSnS4 thin films10.1063/1.4861593 ↗
37. The vibrational properties study of kesterite Cu2ZnSnS4 single crystals by using polarization dependent Raman spectroscopy10.1016/j.optmat.2012.09.031 ↗
38. Cu2Zn1-xCdxSn(Se1-ySy)4 solid solutions as absorber materials for solar cells
39. A low-temperature order-disorder transition in Cu2ZnSnS4 thin films10.1063/1.4863685 ↗
40. Composition dependence of structure and optical properties of Cu2ZnSn(S,Se)4 solid solutions: an experimental study10.1016/j.jallcom.2011.08.099 ↗
41. Study of polycrystalline Cu2ZnSnS4 films by Raman scattering10.1016/j.jallcom.2011.04.097 ↗
42. A 4.92% efficiency Cu2ZnSnS4 solar cell from nanoparticle ink and molecular solution10.1039/C6RA08604G ↗
43. Self-regulation of cu/sn ratio in the synthesis of Cu2ZnSnS4 films10.1021/acs.chemmater.5b00108 ↗
44. Towards the growth of Cu2ZnSn1-xGexS4 thin films by a single-stage process: effect of substrate temperature and composition10.1016/j.solmat.2015.03.004 ↗
45. Bulk and surface characteristics of co-electrodeposited Cu2FeSnS4 thin films sulfurized at different annealing temperatures10.1016/j.jallcom.2022.164379 ↗
46. Investigation of Kesterite to stannite phase transition and band gap engineering in Cu2Zn1-XCoxSnS4 thin films prepared by Sol-Gel spin coating10.1016/j.apsusc.2024.160848 ↗
47. Investigation of structural and optical properties of Mg doped ZnS thin films prepared by Mist-CVD technique: experimental and theoretical aspects10.1016/j.matchemphys.2023.128707 ↗
48. A novel one-step electrodeposition to prepare single-phase CuInS2 thin films for solar cells10.1016/j.solmat.2010.10.025 ↗
49. The oxidation states of copper and iron in mineral sulfides, and the oxides formed on initial exposure of chalcopyrite and bornite to air10.1016/j.gca.2006.02.007 ↗
50. Raman and X-ray photoemission identification of colloidal metal sulfides as potential secondary phases in Nanocrystalline Cu2ZnSnS4 photovoltaic absorbers10.1021/acsanm.0c00910 ↗
51. New properties of Fe3O4@SnO2 core shell nanoparticles following interface charge/spin transfer10.1016/j.apsusc.2017.07.267 ↗
52. XPS study of CZTSSe monograin powders10.1016/j.tsf.2010.12.165 ↗
53. Evolution of Na - S(- O) compounds on the Cu2ZnSnS4 absorber surface and their effects on CdS thin film growth10.1021/acsami.6b04978 ↗
54. Facile solution deposition of Cu2ZnSnS4 (CZTS) nano-worm films on FTO substrates and its photoelectrochemical property10.1016/j.apsusc.2015.12.065 ↗
55. Structural, electronic, and optical properties of Cu2NiSnS4: a combined experimental and theoretical Study toward photovoltaic applications10.1021/acs.chemmater.7b00149 ↗
56. Effect of the order-disorder transition on the seebeck coefficient of nanostructured thermoelectric Cu2ZnSnS410.3390/nano9050762 ↗
57. A low-cost, ligand exchange-free strategy to synthesize large-grained Cu2ZnSnS4 thin-films without a fine-grain underlayer from nanocrystals10.1039/C5TA03640B ↗
58. A wide-band-gap p -type thermoelectric material based on quaternary chalcogenides of Cu2ZnSnQ4 (Q=S,Se)10.1063/1.3130718 ↗
59. Towards low cost and sustainable thin film thermoelectric devices based on Quaternary chalcogenides10.1002/adfm.202202157 ↗
60. Structural and transport properties of Cu2CoSnS4 films prepared by spray pyrolysis10.1016/j.ceramint.2022.07.185 ↗
61. Electrical properties of CuxZnySnS4 films with different Cu/Zn ratios10.1016/j.tsf.2013.10.134 ↗
62. The inclusion of ceramic carbides dispersion in In and Yb filled CoSb3 and their effect on the thermoelectric performance10.1016/j.jallcom.2021.162400 ↗
63. Surface polarization enhanced Seebeck effects in vertical multi-layer metal-polymer-metal thin-film devices10.1039/C4CP03603D ↗
64. Facile and low-cost fabrication of Cu/Zn/Sn-Based ternary and Quaternary chalcogenides thermoelectric generators10.1021/acsaem.2c00268 ↗
65. Influence of the synthesis parameters on the transport properties of Mg2Si0.4Sn0.6 solid solutions produced by melting and spark plasma sintering10.1016/j.jpcs.2021.110561 ↗
66. Thermoelectric properties of p-type Mg2Si0.3Sn0.7 doped with silver and gallium10.1016/j.jallcom.2023.169270 ↗
67. The thermoelectric properties of bulk crystalline n- and p-type Mg2Si prepared by the vertical Bridgman method10.1063/1.2946722 ↗