Photoluminescence enhancement of novel K(Y,Lu)CaWO6: Eu3+ red phosphor prepared by controllable citrate-EDTA complexing method

Abstract Novel double-perovskite K(Y0.95-xLuxEu0.05)CaWO6 red phosphors were successfully prepared by the controllable citrate-EDTA complexing method. XRD with structure refinement, FTIR, Raman and photoluminescence spectra were combined to systematically investigate the structure parameters and luminescence properties of prepared phosphors. The substitution of Lu3+ with smaller ionic radius resulted in the lower symmetry even with the same space group of C2/m, which was also directly observed from the red shift and splitting of Raman T2 g(1) mode. The concentration higher than x = 0.6 made the intensity alteration in the excitation spectra from charge transfer band to 4f−4f of Eu3+. The obvious enhancements of red emission at 615 nm were obtained under both blue and ultraviolet lights, respectively, and reached almost the same intensity at x = 0.6. Meanwhile, the more standard red light could be found by the gradual shifts of CIE chromaticity coordinates and bigger ratio of red/orange emission. The substitution of Lu3+ improved the quality and emission intensity of red light of this double perovskite system and the composition optimized phosphor of K(Y0.35Lu0.6Eu0.05)CaWO6 exhibited great potential in the application of white LEDs.