Experimental research on dynamic response of PZT-5H under impact load

Abstract In order to improve the stability of PZT-based sensors, the mechanical, dielectric, ferroelectric and piezoelectric properties of PZT-5H under impact load were studied experimentally by using the separated Hopkinson pressure bar (SHPB) with an electrical output measurement device. At the same time, the experimental study on the material properties of PZT-5H before and after the impact was carried out. The effect of impact cracks on the output voltage of PZT-5H was also analyzed. The results show that the dynamic piezoelectric constants of PZT-5H under low stress impact (10–50 MPa) are different from those under quasi-static state, and the empirical relationship between them and the peak stress is obtained through experiments. The dielectric properties of PZT-5H did not change under low stress impact, but micro-cracks occurred in the material and dielectric loss increased at high frequencies. Under short circuit, the residual polarization intensity of PZT-5H decreases sharply due to impact load. While the impact load causes the secondary polarization and the increase of the residual polarization intensity of PZT under open circuit. When the stress is over 45 MPa, the PZT-5H breaks. The formation of cracks causes abnormal discharge voltage and gap discharge.