Large electric-field-induced strain in B-site complex-ion (Fe0.5Nb0.5)4+-doped Bi1/2 (Na0.82K0.12)1/2TiO3 lead-free piezoceramics

Abstract In order to obtain a new system of (Bi 1/2 Na 1/2 )TiO 3 (BNT) based lead-free incipient piezoceramics with large strain for practical applications of actuators, we investigated the effect of B-site complex-ion (Fe 0.5 Nb 0.5 ) 4+ (FN)-doped Bi 1/2 (Na 0.82 K 0.12 ) 1/2 TiO 3 ceramics on the phase structure, dielectric, ferroelectric, piezoelectric and electric-field-induced strain properties. All samples exhibited single perovskite phase with pseudocubic symmetry. The room temperature electric-field-induced polarization ( P - E ) and strain ( S - E ) hysteresis loops indirectly illustrated ferroelectric-to-relaxor (FE-RE) phase transition. The increasing content of FN doping decreased the FE-RE phase transition temperature, T F-R to below room temperature and induced the reversible FE-RE phase transition, giving rise to a large strain of 0.462% with a normalized strain, d * 33 of 660 pm/V at a critical composition of x = 5. A fluctuation of the dielectric curve for BNKT-5 mol% FN ceramics in the spectra around 80 °C before and after polarization suggested that the large strain response can be induced via delicate mixing of the FE and RE phase.