Tin Oxide as a Protective Heterojunction with Silicon for Efficient Photoelectrochemical Water Oxidation in Strongly Acidic or Alkaline Electrolytes

Abstract Photoelectrodes without a p–n junction are often limited in efficiency by charge recombination at semiconductor surfaces and slow charge transfer to electrocatalysts. This study reports that tin oxide (SnO_x) layers applied to n‐Si wafers after forming a thin chemically oxidized SiO_x layer can passivate the Si surface while producing ≈620 mV photovoltage under 100 mW cm⁻² of simulated sunlight. The SnO_x layer makes ohmic contacts to Ni, Ir, or Pt films that act as precatalysts for the oxygen‐evolution reaction (OER) in 1.0 m KOH(aq) or 1.0 m H₂SO₄(aq). Ideal regenerative solar‐to‐O₂(g) efficiencies of 4.1% and 3.7%, respectively, are obtained in 1.0 m KOH(aq) with Ni or in 1.0 m H₂SO₄(aq) with Pt/IrO_x layers as OER catalysts. Stable photocurrents for >100 h are obtained for electrodes with patterned catalyst layers in both 1.0 m KOH(aq) and 1.0 m H₂SO₄(aq).