Surface & grain boundary co-passivation by fluorocarbon based bifunctional molecules for perovskite solar cells with efficiency over 21%
Source abstract
Abstract
An effective strategy of surface & grain boundary co-passivation is demonstrated to access perovskite solar cells with 21.31% champion efficiency as well as a highly improved stability of less than 3% efficiency loss after 2500 hours at a humidity of 70%.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Perovskite Materials and Applications · Quantum Dots Synthesis And Properties · Chalcogenide Semiconductor Thin Films
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
State Key Laboratory of Solidification Processing
Center for Nano Energy Materials
School of Materials Science and Engineering
Northwestern Polytechnical University
Shaanxi Joint Laboratory of Graphene (NPU)
Stephenson Institute for Renewable Energy
Department of Chemistry
University of Liverpool
Liverpool
UK
Funding
National Natural Science Foundation of China · Natural Science Foundation of Shaanxi Province
References (51)
Show source-provided references
1. Chen · Nature · 2017 · 550 · 9210.1038/nature23877 ↗
2. Shin · Science · 2017 · 356 · 16710.1126/science.aam6620 ↗
3. Tan · Science · 2017 · 355 · 72210.1126/science.aai9081 ↗
4. Yang · Science · 2017 · 356 · 137610.1126/science.aan2301 ↗
5. National Center for Photovoltaics (NCPV) at the National Renewable Energy Laboratory (NREL); www.nrel.gov/pv/assets/images/efficiency-chart-20180716.jpg
6. Dong · Science · 2015 · 347 · 96710.1126/science.aaa5760 ↗
7. Dequilettes · Science · 2015 · 348 · 68310.1126/science.aaa5333 ↗
8. Shi · Science · 2015 · 347 · 51910.1126/science.aaa2725 ↗
9. Azpiroz · Energy Environ. Sci. · 2015 · 8 · 211810.1039/C5EE01265A ↗
10. Wang · Energy Environ. Sci. · 2017 · 10 · 51610.1039/C6EE02941H ↗
11. Wang · Adv. Mater. · 2016 · 28 · 998610.1002/adma.201603062 ↗
12. Zheng · Nat. Energy · 2017 · 2 · 1710210.1038/nenergy.2017.102 ↗
13. Noel · ACS Nano · 2014 · 8 · 981510.1021/nn5036476 ↗
14. Fu · Chem. Commun. · 2017 · 53 · 182910.1039/C6CC09492A ↗
15. Wang · J. Phys. Chem. C · 2017 · 121 · 156210.1021/acs.jpcc.6b12137 ↗
16. deQuilettes · ACS Nano · 2017 · 11 · 1148810.1021/acsnano.7b06242 ↗
17. Mamun · Phys. Chem. Chem. Phys. · 2017 · 19 · 914310.1039/C7CP01140G ↗
18. Simpson · J. Phys. Chem. Lett. · 2017 · 8 · 329910.1021/acs.jpclett.7b01368 ↗
19. Merdasa · ACS Nano · 2017 · 11 · 531910.1021/acsnano.6b07407 ↗
20. Mastroianni · Nanoscale · 2015 · 7 · 1965310.1039/C5NR05308K ↗
21. Draguta · J. Phys. Chem. Lett. · 2016 · 7 · 71510.1021/acs.jpclett.5b02888 ↗
22. Shao · Energy Environ. Sci. · 2016 · 9 · 175210.1039/C6EE00413J ↗
23. De Marco · Nano Lett. · 2016 · 16 · 100910.1021/acs.nanolett.5b04060 ↗
24. Chu · Nat. Commun. · 2017 · 8 · 223010.1038/s41467-017-02331-4 ↗
25. Yun · J. Phys. Chem. Lett. · 2015 · 6 · 87510.1021/acs.jpclett.5b00182 ↗
26. Jodlowski · Nat. Energy · 2017 · 2 · 97210.1038/s41560-017-0054-3 ↗
27. Xu · Nat. Commun. · 2015 · 6 · 708110.1038/ncomms8081 ↗
28. Li · Nat. Chem. · 2015 · 7 · 70310.1038/nchem.2324 ↗
29. Bi · Adv. Mater. · 2016 · 28 · 291010.1002/adma.201505255 ↗
30. Chen · Nano Lett. · 2014 · 14 · 415810.1021/nl501838y ↗
31. Liu · Nano Energy · 2016 · 30 · 41710.1016/j.nanoen.2016.10.036 ↗
32. Shao · Nat. Commun. · 2014 · 5 · 578410.1038/ncomms6784 ↗
33. Guo · J. Am. Chem. Soc. · 2017 · 139 · 959810.1021/jacs.7b03856 ↗
34. Lee · ACS Energy Lett. · 2018 · 3 · 64710.1021/acsenergylett.8b00121 ↗
35. Liu · Adv. Mater. · 2018 · 30 · 180054410.1002/adma.201800544 ↗
36. Bi · Nat. Energy · 2016 · 1 · 1614210.1038/nenergy.2016.142 ↗
37. Niu · Adv. Mater. · 2018 · 30 · 170657610.1002/adma.201706576 ↗
38. Guo · J. Mater. Chem. A · 2018 · 6 · 591910.1039/C8TA00583D ↗
39. Zuo · Sci. Adv. · 2017 · 3 · e170010610.1126/sciadv.1700106 ↗
40. Rothmann · Nat. Commun. · 2017 · 8 · 1454710.1038/ncomms14547 ↗
41. Alberti · ChemPhysChem · 2015 · 16 · 306410.1002/cphc.201500374 ↗
42. Zhao · Nat. Commun. · 2016 · 6 · 1022810.1038/ncomms10228 ↗
43. Wei · Nano Energy · 2016 · 26 · 13910.1016/j.nanoen.2016.05.023 ↗
44. Cha · J. Am. Chem. Soc. · 2016 · 138 · 858110.1021/jacs.6b04519 ↗
45. Cho · Science · 2015 · 350 · 122210.1126/science.aad1818 ↗
46. Bi · Sci. Adv. · 2016 · 2 · e150117010.1126/sciadv.1501170 ↗
47. Li · Energy Environ. Sci. · 2017 · 10 · 123410.1039/C7EE00358G ↗
48. Lindblad · J. Phys. Chem. Lett. · 2014 · 5 · 64810.1021/jz402749f ↗
49. Wang · Energy Environ. Sci. · 2016 · 10 · 51610.1039/C6EE02941H ↗
50. Saliba · Science · 2016 · 354 · 20610.1126/science.aah5557 ↗
51. Saliba · Energy Environ. Sci. · 2016 · 9 · 198910.1039/C5EE03874J ↗