Degradation-induced energy level mismatch in cohost-dopant blue phosphorescent OLEDs after device operation

Phosphorescent organic light emitting diodes PhOLEDs have been considered potential candidates for high efficiency blue emission. However, their short lifetime has been an issue, and much effort has been put into resolving this. Among such efforts, understanding energy level alignments ELA is one of the essential factors in understanding the degradation. However, ELA inside the actual PhOLED is rarely studied due to technical limitations. Here, we comprehensively investigate the degradation mechanism of blue PhOLEDs consisting of a cohost dopant type emissive layer EML . The blue PhOLEDs are aged with typical operating conditions until the luminance performance degrades. Ultraviolet and X ray photoelectron spectroscopy UPS and XPS combined with a damage free gas cluster ion beam GCIB etching and transmission electron microscopy energy dispersive X ray spectroscopy TEM EDX unveil the buried interfaces inside the PhOLEDs. XPS and TEM EDX measurements show that the dopant is unlikely to be the primary origin of the device degradation. Instead, UPS measurements show that the ELAs at the interfaces facing the EML are significantly altered unfavorably after device aging. This implies that the changes in the ELA are the leading cause of PhOLED degradation. Our results highlight the importance of retaining the ELAs during device operation to achieve long lifetime blue PhOLEDs