Formation of titania composite coatings on carbon steel by plasma electrolytic oxidation

Abstract Titania composite coatings were prepared on carbon steel by plasma electrolytic oxidation in silicate electrolyte and aluminate electrolyte with titania powers doping in the electrolytes. The microstructure of the coatings was characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The properties of the coatings including bond strength, thickness, thermal shock resistance and corrosion resistance varying with the quantities of titania powers in the electrolytes were studied. Investigation results revealed that the coating obtained in silicate electrolyte was composed of anatase-TiO2, rutile-TiO2 crystal phases and some Fe, Si, P elements; coating obtained in aluminate electrolyte consisted of anatase-TiO2, Al2TiO5 and some Fe, P elements. Coatings obtained in two types of electrolytes show porous and rough surface. With increasing the concentration of titania powers in the electrolytes, the coating surface first became more compact and less porous and then became more porous and coarse. The bond strength and thickness were not strongly affected by concentration of titania powers in electrolytes. The valves were 23 MPa and for 66 μm for coatings obtained in aluminate electrolyte, and 21 MPa and 35 μm for coatings obtained in silicate electrolyte. Coatings obtained in silicate electrolyte showed a little better thermal shock resistance than those obtained in aluminate electrolyte and the best coatings were obtained with middle concentration of titania powers in the electrolytes. All coated samples showed better corrosion resistance than the substrate in 3.5 wt% NaCl solution. The best coatings were also obtained with middle concentration of titania powers doping in both electrolytes whose corrosion current density was decreased by 2 orders of magnitude compared with the substrate.