CuInS2 thin films obtained through the annealing of chemically deposited In2S3–CuS thin films

Abstract In this work, we report the formation of CuInS 2 thin films on glass substrates by heating chemically deposited multilayers of copper sulfide (CuS) and indium sulfide (In 2 S 3 ) at 300 and 350 °C in nitrogen atmosphere at 10 Torr. CIS thin films were prepared by varying the CuS layer thickness in the multilayers with indium sulfide. The XRD analysis showed that the crystallographic structure of the CuInS 2 (JCPDS 27-0159) is present on the deposited films. From the optical analysis it was estimated the band gap value for the CIS film (1.49 eV). The electrical conductivity varies from 3 × 10 −8 to 3 Ω −1 cm −1 depending on the thickness of the CuS film. CIS films showed p-type conductivity.