Effects of ion- and electron-beam treatment on surface physicochemical properties of polylactic acid

Abstract We describe our investigations of the surface physicochemical and mechanical properties of polylactic acid modified by silver, argon and carbon ion implantation to doses of 1 × 10 14 , 1 × 10 15 and 1 × 10 16 ions/cm 2 at energies of 20 keV (for C and Ar) and 40 keV (for Ag), and by electron beam treatment with pulse-width of 100–300 μs in 50 μs increments at a beam energy 8 keV. Carbonyl bonds ( C O) related IR peak was reduced after ion and electron beam irradiation. Molecular weight of PLA decreases twice and does not depend on the nature of the bombarding particles. The microhardness of treated samples decreases by a factor of 1.3, and the surface conductivity increases by 6 orders of magnitude after ion implantation, and increases only modestly after electron beam treatment. Atomic force microscopy shows that surface roughness increases with irradiation dose. Samples irradiated with Ag to a dose of 1 × 10 16 ions/cm 2 show the greatest roughness of 190 nm.