Characterization of in situ synthesized TiB2 reinforcements in iron-based composite coating

Abstract TiB2 reinforced iron-based composite coatings can be fabricated on the mild steel substrate with a powder mixture of Ti and B4C by plasma transferred arc (PTA) powder surfacing process. Characterizations of the TiB2 reinforcements in the coated surface were investigated in this paper. The experimental work enables the following findings to be obtained: (i) acicular shaped and blocky formed TiB2 phases could be synthesized in situ using PTA powder surfacing process in the iron-based composite coating. (ii) Gradient distributions of TiB2 reinforcements appeared in the composite coating from both the vertical and horizontal direction of the coating's cross-section. Significant changes of the size, shape and volume fraction for TiB2 particles appeared in different regions of the surface coating, due to the effects of the dilution rate and mass density. (iii) Values of coating dilution could have profound impacts on the characterization of TiB2 reinforcements in the coated surfaces. With the increase of coating dilution, TiB2 grain tends to be acicular shaped at the edge of the surface coating, while it remains to be granular formed in the center of the composite coating.