Thermal stability of HfO2 nanotube arrays

Abstract Thermal stability of highly ordered hafnium oxide (HfO 2 ) nanotube arrays prepared through an electrochemical anodization method in the presence of ammonium fluoride is investigated in a temperature range of room temperature to 900 °C in flowing argon atmosphere. The formation of the HfO 2 nanotube arrays was monitored by current density transient characteristics during anodization of hafnium metal foil. Morphologies of the as-grown and post-annealed HfO 2 nanotube arrays were analyzed by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Although monoclinic HfO 2 is thermally stable up to 2000 K in bulk, the morphology of HfO 2 nanotube arrays degraded at 900 °C. A detailed X-ray photoelectron spectroscopy (XPS) study revealed that the thermal treatment significantly impacted the composition and the chemical environment of the core elements (Hf and O), as well as F content coming from the electrolyte. Possible reasons for the degradation of the nanotube at high temperature were discussed based on XPS study and possible future improvements have also been suggested. Moreover, dielectric measurements were carried out on both the as-grown amorphous film and 500 °C post-annealed crystalline film. This study will help us to understand the temperature impact on the morphology of nanotube arrays, which is important to its further applications at elevated temperatures.