Room temperature near-field photoluminescence of zinc-blend and wurtzite ZnO structures

Abstract Near-field photoluminescence (PL) was measured from ZnO film, composed of nanocrystallites with zinc-blend (ZB) and wurtzite (W) structures, on a sapphire (0 0 0 1) substrate at room temperature (RT). The size of nanocrystallites was in the range of 30–50 nm. Using a fiber probe with aperture size of 80 nm, two near-field emission peaks attributed to one ZB and one W structures were observed. The difference in the emission energies was 0.10 eV close to the calculated bandgap difference between ZB and W structures. The intensity of emission peak from ZB structure with lower energy was stronger than that from W structure, which is supposed to be resulted from the quenched excitonic effect of W structure.