Electronic properties of the surface of perylene tetracarboxylic acid dianhydride film upon deposition of the ultrathin conjugated layers of Pyronine B

Abstract Ultrathin conjugated layers of Pyronine B were thermally deposited in UHV on the surface of perylene tetracarboxylic acid dianhydride (PTCDA) film. The structure of unoccupied electron states located 5–20 eV above the Fermi level ( E F ) and the surface potential were monitored during the Pyronine B overlayer deposition, using an incident beam of low-energy electrons according to the total current electron spectroscopy (TCS) method. Electronic work function of the PTCDA surface changed from 4.9 ± 0.1 eV, during the Pyronine B deposition due to the change of the contents of the surface layer, until it reached a stable value 4.6 ± 0.1 eV at the Pyronine B film thickness 8–10 nm. The interface dipole corresponds to electron transfer from the Pyronine B overlayer to the PTCDA surface and the polarization in the Pyronine B overlayer was found confined within approximately 1 nm near the interfaces. The edges of major bands of density of unoccupied electronic states (DOUS) of PTCDA substrate and of the Pyronine B overlayer were unaffected by the process of the interface formation. The major TCS spectral features of the Pyronine B film corresponding to the DOUS band edges were identified and the assignment of the π * , σ * (C–C) and σ * (C C) character was suggested.