Bonding of Cf/SiC composite to Invar alloy using an active cement, Ag–Cu eutectic and Cu interlayer
Source abstract
Abstract
Abstract The interfacial microstructures and mechanical properties of the joints formed by active cement added brazing in vacuum of C f /SiC composite to Invar alloy, using Ag–Cu eutectic alloy and pure copper foil as braze alloy and interlayer respectively, were investigated. CuTi, Cu 4 Ti 3 , Fe 2 Ti and the reaction layer of TiC and Si were the predominant components at the joint interface. The maximum shear strength of the joint was 77 MPa for brazing at 850 °C for 15 min. The results show that active cement added brazing in vacuum using Ag–Cu eutectic alloy and Cu interlayer can be used successfully for joining C f /SiC composites to Invar alloy.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Aluminum Alloys Composites Properties · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (10)
Show source-provided references
1. Advanced ceramic matrix composite materials for current and future propulsion technology applications10.1016/j.actaastro.2004.05.052 ↗
2. Effect of fiber architectures on thermal cycling damage of C/SiC composites in oxidizing atmosphere10.1016/j.msea.2007.02.104 ↗
3. Brazing of ceramic-matrix composites to Ti and Hastealloy using Ni-base metallic glass interlayers10.1016/j.msea.2007.11.150 ↗
4. Influence of the strain rate on the mechanical behavior of the 3D needle-punched C/SiC composite10.1016/j.msea.2009.01.024 ↗
5. Non-destructive testing of satellite nozzles made of carbon fibre ceramic matrix composite, C/SiC10.1016/j.matchar.2006.09.010 ↗
6. Joining of 3D C/SiC composites to niobium alloy10.1016/j.scriptamat.2006.03.050 ↗
7. Joining of partially sintered alumina to alumina, titanium, Hastealloy and C–SiC composite using Ag–Cu brazes10.1016/j.jeurceramsoc.2007.06.017 ↗
8. A comparison of oven-cured and induction-cured adhesively bonded composite joints10.1177/0021998303037006776 ↗
9. Brazing of carbon fiber reinforced SiC composite and TC4 using Ag–Cu–Ti active brazing alloy10.1016/j.msea.2009.09.024 ↗
10. Pressureless brazing of zirconia to stainless steel with Ag–Cu filler metal and TiH2 powder10.1016/j.jeurceramsoc.2008.04.008 ↗