The use of trivalent chromium bath to obtain a solar selective black chromium coating
Source abstract
Abstract
Abstract Black chromium coatings were electrodeposited from a trivalent chromium bath using a ZnO additive as a second main component. Black chromium was electrodeposited on steel and copper plates and substrates plated with bright nickel prior to black chromium electrodeposition. The black chromium coatings were characterized by XRD and SEM. The XRD data suggest that the phase structure of black chromium may be defined as a zinc solid solution in chromium or a chromium solid solution in zinc depending on the chromium/zinc ratio in the deposit. The role of substrate finish was evaluated through the corrosion resistance and reflectance of black chromium. According to corrosion tests the samples plated with bright nickel prior to black chromium deposition have shown the highest corrosion resistance. The electrodeposited black chromium possesses good optical properties for the absorption of solar energy. The absorption coefficient of black chromium was found to be over 0.99 for the samples obtained without the Ni undercoat and below 0.99 for those obtained with the use of Ni undercoat. However, the use of nickel undercoat before black chromium plating is recommended because it remarkably improves the corrosion resistance of samples.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Solar Thermal and Photovoltaic Systems · Thin-Film Transistor Technologies · High-Temperature Coating Behaviors
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. Lee · Sol. Energy Mater. Sol. Cells · 1993 · 29 · 14910.1016/0927-0248(93)90073-C ↗
2. Drivers · Sol. Energy · 1977 · 19 · 30110.1016/0038-092X(77)90074-3 ↗
3. Lampert · Proc. SPIE · 1978 · 161 · 8410.1117/12.956876 ↗
4. Zajac · J. Appl. Phys. · 1980 · 51 · 554410.1063/1.327475 ↗
5. Lee · Sol. Energy Mater. Sol. Cells · 2000 · 63 · 12510.1016/S0927-0248(99)00164-6 ↗
6. Sweet · Sol. Energy Mater. · 1984 · 10 · 25110.1016/0165-1633(84)90034-0 ↗
7. Smith · Sol. Energy Mater. · 1983 · 9 · 2110.1016/0165-1633(83)90028-X ↗
8. Smith · Surf. Sci. · 1982 · 114 · 61410.1016/0039-6028(82)90709-9 ↗
9. Smith · Sol. Energy Mater. · 1980 · 2 · 46210.1016/0165-1633(80)90040-4 ↗
10. Anandan · Appl. Surf. Sci. · 2002 · 191 · 25410.1016/S0169-4332(02)00192-7 ↗
11. Lee · J. Korean Phys. Soc. · 2007 · 51 · 13510.3938/jkps.51.135 ↗
12. Rajagopalan · J. Inst. Metals · 1964 · 93 · 129
13. Rajagopalan · J. Electroanal. Chem. · 1965 · 10 · 465
14. Lampert · Thin Solid Films · 1980 · 72 · 7310.1016/0040-6090(80)90560-X ↗
15. Ignatiev · Sol. Energy Mater. · 1979 · 1 · 6910.1016/0165-1633(79)90058-3 ↗
16. Bacon · Sol. Energy Mater. · 1983 · 9 · 310.1016/0165-1633(83)90027-8 ↗
17. Quintana · Sol. Energy Mater. Sol. Cells · 1994 · 33 · 46510.1016/0927-0248(94)90006-X ↗
18. Khamlich · J. Phys. Chem. Solids · 2011 · 72 · 71410.1016/j.jpcs.2011.02.015 ↗
19. Khamlich · Appl. Surf. Sci. · 2013 · 265 · 74510.1016/j.apsusc.2012.11.099 ↗
20. Khamlich · Nanosci. Nanotechnol. Lett. · 2011 · 3 · 55010.1166/nnl.2011.1217 ↗
21. Khamlich · Physica B · 2012 · 407 · 150910.1016/j.physb.2011.09.073 ↗
22. T. Shikata, S. Veda, M. Inagaki, US Patent No. 4262060, 14 April 1981.
23. H. Gutwein, E. Erben, A. Muhlratzer, B. Cornils, B. Tihanyi, W. Dewin, US Patent No. 4473447, 25 September 1984.
24. Bayati · Renew. Energy · 2005 · 30 · 216310.1016/j.renene.2005.02.003 ↗
25. Surviliene · Russ. J. Electrochem. · 1997 · 33 · 418
26. Surviliene · Zashchita metallov · 1998 · 34 · 402
27. LST EN ISO 9227:2012, Corrosion tests in artificial atmospheres – Salt spray tests.
28. Sirviliene · J. Appl. Electrochem. · 2006 · 36 · 64910.1007/s10800-005-9105-8 ↗
29. Moser · J. Phase Equilib. · 1992 · 13 · 17210.1007/BF02667482 ↗