Correlation between interfacial interactions and mechanical properties of PA-6 doped with surface-capped nano-silica

Abstract The polyamide-6 pellets were mixed with nano-SiO2 particles surface-capped by 3-aminopropyltriethoxysilane (APS) via a melt blending route. PA-6 composites doped with surface-capped nano-SiO2 (designated as PAMNS, where AMNS refers to APS surface-capped nano-SiO2). AMNS and the silica samples (designated as EAMNS) extracted by acid etching from various PAMNS samples containing different concentration of amino functional groups on surface-capped nano-silica surfaces were characterized by means of Fourier transformation infrared spectrometry (FTIR), X-ray photoelectron spectroscopy (XPS) and thermogravimetric analysis (TGA). This aims at revealing the interfacial interaction between AMNS and PA-6 matrix and its effect on the mechanical properties of the filled PA-6 composites. The chemical features and microstructures of the PAMNS composites were analyzed by means of FTIR and transmission electron microscopy (TEM), respectively, while their mechanical properties were evaluated using standardized test rigs. Results demonstrate that the surface-modified nano-SiO2 particles were uniformly dispersed in PA-6 matrix. The residue silica extracted from various PAMNS samples showed characteristic FTIR absorbance peak of PA-6 and had larger weight losses than AMNS, implying that the polymeric matrix was chemically bonded with the nanofiller particles. The interfacial interactions are closely related to the concentration of functional groups in AMNS, and there might exist a critical concentration at which the strongest interfacial interactions could be reached. Beyond the critical concentration of the functional groups in AMNS, the mechanical properties of the filled PA-6 composites tended to decrease to some extent.