The effect of fluorine-based plasma treatment on morphology and chemical surface composition of biocompatible silicone elastomer

Abstract X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) have been used to investigate the effect of reactive ion etching (RIE) on poly(methylhydrogensiloxane-co-dimethylsiloxane) surface in fluorine-based plasmas. Polysiloxane layers supported on the standard silicon wafers were etched using SF 6 + O 2 or CF 4 + O 2 plasmas. SEM studies show that the polysiloxane morphology depends on plasma chemical composition strongly. Presence of a columnar layer likely covered with a fluorine rich compound was found on the elastomer surface after the CF 4 + O 2 plasma exposure. After the SF 6 + O 2 or CF 4 + O 2 plasma treatment the polysiloxane surface enriches with fluorine or with fluorine and aluminum, respectively. Different morphologies and surface chemical compositions of the silicone elastomer etched in both plasmas indicate different etching mechanisms.