Nanomechanical characteristics of SnO2:F thin films deposited by chemical vapor deposition

The nanoindentation characterizations and mechanical properties of fluorine-doped tin oxide (SnO2:F) films deposited on glass substrates, using chemical vapor deposition (CVD) method, were studied, which included the effects of the indentation loads, the loading time and the hold time on the thin film. The surface roughness, fractal dimension and frictional coefficient were also studied by varying the freon flow rates. X-ray diffraction (XRD), atomic force microscopy (AFM) and frictional force microscopy (FFM) were used to analyze the morphology of the microstructure. The results showed that crystalline structure of the film had a high intensity (1 1 0) peak orientation, especially at a low freon flow rate. According to the nanoindentation records, the Young’s modulus ranged from 62.4 to 75.1 GPa and the hardness ranged from 5.1 to 9.9 GPa at a freon flow rate of 8000 sccm. The changes in measured properties were due to changing loading rate. # 2005 Elsevier B.V. All rights reserved.