Fractal analysis and atomic force microscopy measurements of surface roughness for Hastelloy C276 substrates and amorphous alumina buffer layers in coated conductors

Abstract In coated conductors, surface roughness of metallic substrates and buffer layers could significantly affect the texture of subsequently deposited buffer layers and the critical current density of superconductor layer. Atomic force microscopy (AFM) is usually utilized to measure surface roughness. However, the roughness values are actually relevant to scan scale. Fractal geometry could be exerted to analyze the scaling performance of surface roughness. In this study, four samples were prepared, which were electro polished Hastelloy C276 substrate, mechanically polished Hastelloy C276 substrate and the amorphous alumina buffer layers deposited on both the substrates by ion beam deposition. The surface roughness, described by root mean squared (RMS) and arithmetic average ( R a ) values, was analyzed considering the scan scale of AFM measurements. The surfaces of amorphous alumina layers were found to be fractal in nature because of the scaling performance of roughness, while the surfaces of Hastelloy substrates were not. The flatten modification of AFM images was discussed. And the calculation of surface roughness in smaller parts divided from the whole AFM images was studied, compared with the results of actual AFM measurements of the same scan scales.