Preparation and microstructure characteristics of low-temperature bainite in surface layer of low carbon gear steel

Abstract A kind of technology was proposed for the development of low-temperature bainitic microstructure in the surface layer of low-carbon gear steel 20CrMnMo, which is based on carburization and succedent low-temperature austempering. The carbon content in the surface carburization layer increases to 0.81 wt.%, making the martensite starting point depressed. Low-temperature bainite formed in the carburization layer and lath martensite with low carbon content in the center by austempering at a low temperature slightly higher than the martensite starting point of the surface layer. Aluminum is added as alloying elements with the purpose of enhancing the driving force of bainitic transformation and retarding the precipitation of cementite during austempering. With the excellent toughness of low-temperature bainite, this low-temperature austempering technology could be a potential substitute of the traditional quenching and tempering heat treatment in the manufacture of gear.