Synthesis and optical characterization of vertically grown ZnO nanowires in high crystallinity through vapor–liquid–solid growth mechanism

Abstract The gas-phase growth and optical characteristics of 1-dimensional ZnO nanostructure have been investigated. The ZnO nanowires (NWs) were grown vertically on Au coated silicon substrates by vapor–liquid–solid (VLS) growth mechanism using chemical vapor deposition (CVD). The ZnO NWs were grown in the crystal direction of [0 0 0 1]. The ZnO NWs exhibit the uniform size of less than 100 nm in diameter and up to 5 μm in length. Photoluminescence (PL) spectrum of ZnO NWs shows the strong band-edge emission at ∼380 nm (∼3.27 eV) without significant deep-level defect emission. The exciton lifetime of ZnO NWs was measured to be approximately 150 ± 10 ps.