Fabrication and characterization of sputtered titanium dioxide films

Abstract TiO2 thin films were prepared under various conditions by using a reactive RF sputtering technique. The structural, optical and electrical characteristics of the films have been investigated. All as-deposited films were amorphous. After annealing at T > 673 K, the crystallinity of the observed tetragonal anatase phase appeared improved. The optical band gap, determined by using Tauc plot, has been found to amount to 3.38 ± 0.03 and 3.21 ± 0.03 eV for the direct and indirect transition, respectively. Also the complex optical constants for the wavelength range 300–2500 nm are reported. Using the two-point probe technique, the dark resistivity has been measured as a function of the film thickness, d. The resistivity, ρ, of the samples has been found to decrease markedly with increasing thickness, but only for d