Large lattice mismatch of nanocomposite coating: In-situ establishment of MoS2 by precursor and desulfurization reaction

Constructing large lattice mismatch interfaces, especially two-dimensional materials such as MoS 2 , is the key to reaching the structural lubricity of heterogeneous structures. Large lattice mismatch prevents the nucleation of reinforcement of composite material, such as in situ synthesized MoS 2 during the PEO process, thus affecting the mechanical performance. In this work, a precursor reaction, which can form an amorphous MoS 3 /TiO 2 mixtures, is proposed, and the MoS 2 /TiO 2 noncoherent interface with large mismatch is obtained through solid-state in situ desulfurization of suspended S with the action of reheat. Meanwhile, the precursor reaction is strongly dependent on the sulfur source concentration, which can form the interface with a large number of interfacial dislocations by regulating the concentration of sulfur source. Such edge pining noncoherent interface enables more dislocation and distortion near interface during scratch, which reduces the twist-angle dependence thus further improving the tribological properties. Additionally, these results render the herein presented amorphous precursor reaction strategy generally applicable for exhibiting broad application of in situ synthesis of reinforcement.