Ultrathin g-C3N4 films supported on Attapulgite nanofibers with enhanced photocatalytic performance

Abstract A novel visible-light-responsive photocatalyst is fabricated by introducing g-C3N4 ultrathin films onto the surface of attapulgite (ATP) via a simple in-situ depositing technique, in which ATP was pre-grafted using (3-Glycidyloxypropyl) trimethoxysilane (KH560) as the surfactant. A combination of XRD, FT-IR, BET, XPS, UV–vis, TEM and SEM techniques are utilized to characterize the composition, morphology and optical properties of the products. The results show that with the help of KH560, g-C3N4 presented as ultrathin layer is uniformly loaded onto the surface of ATP by forming a new chemical bond (Si O C). Comparing with g-C3N4 and ATP, ATP/g-C3N4 exhibits remarkably enhanced visible-light photocatalytic activity in degradation of methyl orange (MO) because of its high surface area, appropriate band gap and the synergistic effect between g-C3N4 and ATP. To achieve the best photocatalyst, the ratio of g-C3N4 was adjusted by controlling the mass portion between ATP-KH560 and melamine (r = m (ATP-KH560)/m (melamine)). The highest decomposition rate of methyl orange (MO) was 96.06% when r = 0.5 and this degradation efficiency remained unchanged after 4 cycles, which is 10 times as that of pure g-C3N4 particles. Possible photocatalytic mechanism is presented.