Organic modification of TEOS based silica aerogels using hexadecyltrimethoxysilane as a hydrophobic reagent

Abstract The experimental results on the synthesis and characterization of tetraethoxysilane (TEOS) based hydrophobic silica aerogels using hexadecyltrimethoxysilane (HDTMS) as a hydrophobic reagent by two step sol–gel process, are described. The molar ratio of tetraethoxysilane (TEOS), methanol (MeOH), acidic water (0.001 M, oxalic acid) and basic water (10 M, NH 4 OH) was kept constant at 1:55:3.25:1.25 and the molar ratio of HDTMS/TEOS (M) was varied from 0 to 28.5 × 10 −2 . The organic modification was confirmed by infrared spectroscopic studies, and the hydrophobicity of the aerogels was tested by the contact angle measurements. The maximum contact angle of 152° was obtained for M = 22.8 × 10 −2 . The aerogels retained the hydrophobicity up to a temperature of 240 °C and above this temperature the aerogels became hydrophilic. The aerogels were characterized by the thermal conductivity, density, contact angle measurements, optical transmission and scanning electron micrographs.