The chemical and microstructural analysis of the adhesive properties of epoxy resin coatings modified using waste glass powder
Source abstract
Abstract
The article presents the results of tests of epoxy resin coatings modified with the addition of waste glass powder. Pull-off strength tests were performed for ground and patch grabbed cementitious substrates. The results showed that the addition of 19.4% of glass powder in the epoxy resin caused an increase of its pull-off strength. A larger amount of glass powder addition increases the density of the epoxy resin coating to a degree that reduces the positive effect of the additive on pull-off strength and makes it difficult to obtain a smooth coating surface. Finally, to confirm the obtained macroscopic results, the samples were subjected to scanning electron microscopy (SEM) microstructural tests, including analysis of the chemical composition and porosity within the interphase between the epoxy resin and substrate. The SEM results confirmed the optimum performance of the sample that had the addition of 19.4% of glass powder in the epoxy resin. For this sample, the porosity was lower than for the reference sample without the addition of waste glass powder. According to the authors, the addition of waste glass powder ensures sufficient pull-off strength without the use of to the mechanical treatment of the substrate and bonding agents.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Innovative concrete reinforcement materials · Concrete Corrosion and Durability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. Analysis of the European Construction Chemicals Market · 2016
2. Inspection and diagnosis of epoxy resin industrial floor coatings10.1061/(ASCE)0899-1561(2008)20:2(128) ↗
3. Evaluation of the adhesion between overlays and substrates in concrete floors: literature survey, recent non-destructive and semi-destructive testing methods, and research gaps10.3390/buildings9090203 ↗
4. Evaluation of the height 3D roughness parameters of concrete substrate and the adhesion to epoxy resin10.1016/j.ijadhadh.2015.12.019 ↗
5. EN 1504:2006. Products and systems for the protection and repair of concrete structures— Definitions, requirements, quality control and evaluation of conformity.
6. Raupach · 2014
7. Czarnecki · 2017
8. Concrete-to-concrete bond strength. Influence of the roughness of the substrate surface10.1016/j.conbuildmat.2004.04.023 ↗
9. Design recommendations for reinforced concrete interfaces based on statistical and probabilistic methods10.1002/suco.201500083 ↗
10. Winkler spring behavior in FE analyses of dowel action in statically loaded RC cracks
11. Friction and cohesion coefficients of composite concrete-to-concrete bond10.1016/j.cemconcomp.2014.10.003 ↗
12. Czarnecki · 2002
13. The effect of texturing of the surface of concrete substrate on the pull-off strength of epoxy resin coating10.3390/coatings9020143 ↗
14. Innovation in construction materials engineering versus sustainable development
15. Effects of carbon nanotube enrichment of epoxy resins on hybrid FRP–FR confinement of concrete10.1016/j.compositesb.2013.09.044 ↗
16. Performance of polymer-modified self-leveling mortars with high polymer–cement ratio for floor finishing10.1016/S0008-8846(02)01057-8 ↗
17. Effects of diacrylate monomers on the bond strength of polymer concrete to wet substrates10.1002/app.12723 ↗
18. Influence of silica fume and metakaolin with two different types of interfacial adhesives on the bond strength of repaired concrete10.1016/j.conbuildmat.2013.10.048 ↗
19. The impact of surface preparation on the bond strength of repaired concrete by metakaolin containing concrete10.1016/j.conbuildmat.2015.01.018 ↗
20. https://ec.europa.eu/ (accessed 08.10.2019).10.1055/a-0829-4431 ↗
21. Properties of concrete modified with mineral additives10.1016/j.conbuildmat.2016.12.215 ↗
22. Durability of mortar using waste glass powder as cement replacement10.1016/j.conbuildmat.2012.04.027 ↗
23. Waste glass powder as partial replacement of cement for sustainable concrete practice10.1016/j.ijsbe.2016.10.005 ↗
24. Recycling of waste glass as a partial replacement for fine aggregate in concrete10.1016/j.wasman.2008.08.012 ↗
25. Utilization of waste glass powder in the production of cement and concrete10.1016/j.conbuildmat.2016.08.016 ↗
26. The effects of waste glass powder usage on polymer concrete properties10.1016/j.conbuildmat.2013.05.023 ↗
27. https://www.pl.weber/files/pl/2018-03/printable_sheet_weber_floor_FLOW.pdf (accessed 08.10.2019).
28. Multi-sensor evaluation of the concrete within the interlayer bond with regard to pull-off adhesion10.1016/j.acme.2017.09.008 ↗
29. Czarnecki · 2017 · 032037
30. Micromechanical properties within the interphase between heterogeneous layers made of cementitious composites10.1016/j.conbuildmat.2019.04.238 ↗
31. The effect of surface treatment on the microstructure of the skin of concrete10.1016/j.apsusc.2017.09.078 ↗
32. Pore segmentation of cement-based materials from backscattered electron images10.1016/j.cemconres.2005.10.006 ↗
33. Environmentally friendly lightweight gypsum-based materials with waste stone dust