Preparation of WO3/g-C3N4 composites and their application in oxidative desulfurization

Abstract WO3/graphitic carbon nitride (g-C3N4) composites were successfully synthesized through direct calcining of a mixture of WO3 and g-C3N4 at 400 °C for 2 h. The WO3 was prepared by calcination of phosphotungstic acid at 550 °C for 4 h, and the g-C3N4 was obtained by calcination of melamine at 520 °C for 4 h. The WO3/g-C3N4 composites were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), and Brunner−Emmett−Teller analysis (BET). The WO3/g-C3N4 composites exhibited stronger XRD peaks of WO3 and g-C3N4 than the WO3 and pure g-C3N4. In addition, two WO3 peaks at 25.7° and 26.6° emerged for the 36% −WO3/g-C3N4 composite. This finding indicated that WO3 was highly dispersed on the surface of the g-C3N4 nanosheets and interacted with the nanosheets, which resulted in the appearance of (012) and (022) planes of WO3. The WO3/g-C3N4 composite also exhibited a larger specific surface area and higher degree of crystallization than WO3 or pure g-C3N4, which resulted in high catalytic activity of the catalyst. Desulfurization experiments demonstrated that the desulfurization rate of dibenzothiophene (DBT) in model oil reached 91.2% under optimal conditions. Moreover, the activity of the catalyst was not significantly decreased after five recycles.