Surface modification of porous poly(tetrafluoraethylene) film by a simple chemical oxidation treatment

Abstract A simple, inexpensive and environmental chemical treatment process, i.e., treating porous poly(tetrafluoroethylene) (PTFE) films by a mixture of potassium permanganate solution and nitric acid, was proposed to improve the hydrophilicity of PTFE. To evaluate the effectiveness of this strong oxidation treatment, contact angle measurement was performed. The effects of treatment time and temperature on the contact angle of PTFE were studied as well. The results showed that the chemical modification decreased contact angle of as-received PTFE film from 133 ± 3° to 30 ± 4° treated at 100 °C for 3 h, effectively converting the hydrophobic PTFE to a hydrophilic PTFE matrix. The changes in chemical structure, surface compositions and crystal structure of PTFE were examined by attenuated total reflection–Fourier transform infrared spectroscopy (ATR–FTIR), X-ray photoelectron spectroscopy (XPS), environmental scanning electron microscopy (ESEM), X-ray diffraction (XRD), respectively. It was found that the F/C atomic ratio decreased from untreated 1.65–0.10 treated by the mixture at 100 °C for 3 h. Hydrophilic groups such as carbonyl (C O) and hydroxyl ( OH) were introduced on the surface of PTFE after treatment. Furthermore, hydrophilic compounds K0.27MnO2·0.54H2O was absorbed on the surface of porous PTFE film. Both the introduction of hydrophilic groups and absorption of hydrophilic compounds contribute to the significantly decreased contact angle of PTFE.